Objectives: The aim was to investigate shear bond strengths and failure modes of four self-etch bonding agents to bovine dentin and enamel and to compare evaluation of data sets with or without exclusion of cohesive failure specimens.
Methods: Composite-cylinders were bonded perpendicularly to bovine dentin and enamel surfaces. Shear-strengths were measured 24 h post-bonding of: Scotchbond Universal® (SBU, 3 M), OptiBond™ XTR (OBXTR, Kerr), OptiBond™ universal (OBU, KaVo-Kerr) and Prime & Bond active® (PBA, Dentsply-Sirona). Analysis of overall data was made via a linear mixed-model. This was repeated after exclusion of specimens associated with cohesive failures.
Results: When both adhesive and cohesive failures were considered, OBU and OBXTR showed comparable dentin and enamel bond strengths, whereas lower strengths were found on enamel for SBU (p < 0.001) and PBA (p = 0.015). For OBXTR higher shear strengths were measured for specimens associated with cohesive failures. When cohesive failures were excluded, the majority of shear bond strengths of adhesive failure specimens were only slightly different from overall results. However, uniquely with OBXTR dramatically lower shear bond strengths were found for dentin substrate.
Significance: After exclusion of cases with cohesive failures OBXTR adhesive fell behind other materials in the sequence of average shear strengths. This did not reflect the actual performance of the material. Therefore, in statistical analysis we do not recommend exclusion of data based on a specific fracture mode.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1016/j.dental.2022.10.003 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Mechanical Properties and Decomposition Behavior of Compression Moldable Poly(Malic Acid)/-Tricalcium Phosphate Hybrid Materials.
Polymers (Basel)
January 2025
Department of Materials and Applied Chemistry, College of Science and Technology, Nihon University, 1-8-14 Kandasurugadai, Chiyoda-ku, Tokyo 101-8308, Japan.
Calcified tissues in living organisms, such as bone, dentin, and enamel, often require surgical intervention for treatment. However, advances in regenerative medicine have increased the demand for materials to assist in regenerating these tissues. Among the various forms of calcium phosphate (CaP), tricalcium phosphate (TCP)-particularly its α-TCP form-stands out due to its high solubility and efficient calcium release, making it a promising candidate for bone regeneration applications.
View Article and Find Full Text PDFLong-Term Oro-Dental Effects of Chemotherapy in a Pediatric Patient: A Case Study and a Proposed Oral Care Protocol.
J Clin Med
January 2025
Department of Oral Biology, Faculty of Dentistry, Naresuan University, Phitsanulok 65000, Thailand.
: Chemotherapy (CMT) in children can disrupt dental development and calcification, causing long-term dental issues, but good dental care and habits can help improve quality of life. This case report examines permanent dental disturbances in a 7-year, 4-month-old girl undergoing CMT, explores the histology of microdontia, and outlines an oral treatment plan for CMT management. : Clinical examination revealed microdontia and a groove crossing the cervical area (chronological hypoplasia), which were assessed using panoramic radiographs and histological analysis.
View Article and Find Full Text PDFPreheated and Injected Bulk-Fill Resin Composites: A Micro-CT Analysis of Internal Voids and Marginal Adaptation in Class II Restorations.
Materials (Basel)
January 2025
Department of Restorative Dentistry, School of Dentistry, Pontifical Catholic University of Rio Grande do Sul, Porto Alegre 90619-900, Brazil.
The aim of this study was to evaluate, in vitro, the void formation and marginal adaptation in Class II cavities restored with preheated and injected bulk-fill resin composites. Eighty third molars received Class II cavities on their mesial and distal surfaces and were randomly distributed into eight groups (n = 10) according to material (Filtek Universal-control, incremental technique; Filtek One Bulk-Fill; Admira Fusion X-tra Bulk-Fill; VisCalor Bulk-Fill) and the temperature of the material (24 °C or 68 °C). The restored teeth were scanned using a SkyScan 1173 microtomograph.
View Article and Find Full Text PDFEffect of Different Working Settings of Sandblasting on Resin Composite Repair Bond Strength.
Materials (Basel)
January 2025
Department of Preventive Dentistry, Periodontology and Cariology, University Medical Center Göttingen, 37075 Göttingen, Germany.
To investigate the effect of different sandblasting settings on the shear bond strength (SBS) in the repair of resin composite, specimens (resin composite, enamel, and dentin; each group = 16) were sandblasted by varying the parameters of air pressure (0.2/0.3/0.
View Article and Find Full Text PDFAdvanced Lasers and Their Applications in Dentistry.
Dent J (Basel)
January 2025
Faculty of Dentistry, The University of Hong Kong, Hong Kong 999077, China.
The development of laser technology has revolutionized dentistry, offering complementary and alternative approaches to traditional techniques. Lasers have been successfully integrated into various dental procedures, enhancing treatment outcomes and patient care. Several types of lasers can increase the acid resistance of enamel, thus preventing caries.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!