High Current Density Oxygen Evolution in Carbonate Buffered Solution Achieved by Active Site Densification and Electrolyte Engineering.

High current density reaching 1 A cm for efficient oxygen evolution reaction (OER) was demonstrated by interactively optimizing electrolyte and electrode at non-extreme pH levels. Careful electrolyte assessment revealed that the state-of-the-art nickel-iron oxide electrocatalyst in alkaline solution maintained its high OER performance with a small Tafel slope in K-carbonate solution at pH 10.5 at 353 K. The OER performance was improved when Cu or Au was introduced into the FeO -modified nanostructured Ni electrode as the third element during the preparation of electrode by electrodeposition. The resultant OER achieved 1 A cm at 1.53 V vs. reversible hydrogen electrode (RHE) stably for 90 h, comparable to those in extreme alkaline conditions. Constant Tafel slopes, apparent activation energy, and the same signatures from operando X-ray absorption spectroscopy among these samples suggested that this improvement seems solely correlated with enhanced electrochemical surface area caused by adding the third element.