Facile Synthesis of Metal Oxide Decorated Carbonized Bamboo Fibers with Wideband Microwave Absorption.

Aiming at the disadvantages of high cost, complex processes, low yield, and narrow bandwidth of carbon-based microwave absorbing materials, this paper provides a novel and efficient method for synthesizing metal oxide/carbonized bamboo fibers using renewable natural bamboo fibers as a carbon source. The results suggested that the metal oxides such as NiO and FeO were uniformly dispersed on the carbonized bamboo fibers and proved that the dielectric component NiO and magnetic component FeO can significantly improve the microwave absorption performance of the carbonized bamboo fibers. As expected, the NiO/carbonized bamboo fibers showed excellent microwave absorption performance due to the appropriate complex permittivity, high impedance matching, and attenuation coefficient. A wide effective bandwidth of 6.4 GHz with 2.2 mm thickness is achieved, covering the entire Ku-band. Remarkably, the reflection loss (RL) values less than -10 dB covered the whole X-band at a thickness of 3.0 mm. This work reveals the potential of carbonized bamboo fibers-based composite as an economic and broadband microwave absorbent and offers a new strategy for designing promising microwave absorption materials.