Silver nanoparticles loaded graphene-poly-vinylpyrrolidone composites as an effective recyclable antimicrobial agent.

Silver nanoparticles (AgNPs) are often used as antibacterial agents. Here, graphene-silver nanoparticles (G-Ag) and graphene-silver nanoparticles poly-vinylpyrrolidone (G-AgPVPy) were prepared by chemical reduction and in-situ polymerization of vinylpyrrolidone (VPy). The prepared G-Ag and G-AgPVPy composites were characterized using various techniques. The size of the AgNPs on the graphene surface in the prepared G-Ag and G-AgPVPy composites was measured as ∼20 nm. The graphene sheets size in the G-Ag and G-AgPVPy composites were measured as 6.0-2.0 μm and 4.0-0.10 μm, respectively, which are much smaller than graphene sheets in graphite powder (GP) (10.0-3.0 μm). The physicochemical analysis confirmed the formation of G-Ag and G-AgPVPy composites and even the distribution of AgNPs and PVPy on the graphene sheets. The synthesized composites (G-AgPVPy, G-Ag) exhibited a broad-spectrum antibacterial potential against both Gram-negative and Gram-positive bacteria. The lowest minimum inhibitory concentration (MIC) and minimum bactericidal concentration (MBC) values were calculated as >40 μg/mL using G-Ag and GP, while G-AgPVPy showed as 10 μg/mL against Staphylococcus aureus. Among GP, G-Ag, and G-AgPVPy, G-AgPVPy disturbs the cell permeability, damages the cell walls, and causes cell death efficiently. Also, G-AgPVPy was delivered as a significant reusable antibacterial potential candidate. The MIC value (10 μg/mL) did not change up to six subsequent MIC analysis cycles.