Herein, we systematically studied the effect of various excitation processes on the structural, optical, and magnetic properties of ZnO films implanted with 80 keV Ar, 110 keV Mn, and 190 keV Ag ions. Four different doses of 1 × 10, 1 × 10, 1 × 10, and 2 × 10 ions per cm were used for implantation. It was observed that the structural, optical, and magnetic properties of the implanted samples were dominantly affected at the highest dose of 2 × 10 ions per cm. For lower doses, insignificant changes in these properties were observed. A comparison of various processes involved in the implantation process shows that both the electronic excitation and nuclear excitation processes are responsible for the changes in the structural, optical, and magnetic properties of the implanted ZnO films.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC9577707 | PMC |
| http://dx.doi.org/10.1039/d2ra05430b | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Visualization of porcine and human aqueous humor outflow tract anatomies with transparency enhancement.
Jpn J Ophthalmol
January 2025
Institute for Photon Science and Technology, The University of Tokyo, 7-3-1, Hongo, Bunkyo-ku, Tokyo, 113-8656, Japan.
Purpose: There is no established method for visualizing the three-dimensional (3D) structure of the aqueous humor outflow tract. This study attempted to visualize the 3D structures of porcine and human ocular tissues, particularly the aqueous humor outflow tract using a transparency reagent composed of 2, 2-thiodiethanol.
Study Design: Clinical and experimental.
Guest-Molecule-Induced Glass-Crystal Transition in Organic-Inorganic Hybrid Antimony Halides.
Inorg Chem
January 2025
College of Chemistry and Materials Science, College of Environmental and Resource Sciences, Fujian Provincial Key Laboratory of Advanced Materials Oriented Chemical Engineering, Fujian Normal University, Fuzhou 350007, China.
The glassy state of inorganic-organic hybrid metal halides combines their excellent optoelectronic properties with the outstanding processability of glass, showcasing unique application potential in solar devices, display technologies, and plastic electronics. Herein, by tailoring the organic cation from -phenylpiperazine to dimethylamine gradually, four types of zero-dimensional antimony halides are obtained with various optical and thermal properties. The guest water molecules in crystal (-phenylpiperazine)SbCl·Cl·5HO lead to the largest distortion of the Sb-halogen unit, resulting in the red emission different from the yellow emission of other compounds.
View Article and Find Full Text PDFChoroidal thickness and vascular density after rhegmatogenous retinal detachment.
Acta Ophthalmol
January 2025
Department of Ophthalmology, Stavanger University Hospital, Stavanger, Norway.
Purpose: To study choroidal thickness (CT) and luminal areas of choroidal vessels in the setting of fovea-off rhegmatogenous retinal detachment (RRD).
Methods: Twenty-seven eyes with RRD were prospectively studied before and after pars plana vitrectomy and SF6 tamponade, using swept-source optical coherence tomography (SS-OCT). CT was measured pre- and postoperatively both subfoveally and in attached macular areas.
Effect of In Situ Acid Erosion on Structural and Optical Properties of Nanoparticulated Bisacrylic Resin With Different Surface Treatments.
J Esthet Restor Dent
January 2025
Department of Dental Materials and Prosthodontics, Sao Paulo State University (UNESP), School of Dentistry, Araçatuba, São Paulo, Brazil.
Objective: To evaluate the influence of in situ acid erosion on the structural and optical properties of nanoparticulate bisacrylic resin with different surface treatments, evaluating surface roughness (Ra), knoop microhardness (KHN), color change (ΔE, ΔL, ΔC, ΔH), contrast (CR) and translucency (TP).
Methods: Eighty specimens were made (n = 10 per group) and the following surface treatments were applied: U-unpolished; A-polishing with Astropol rubber tips (Ivoclar); S-Biscover LV surface sealant (Bisco) and S-Palaseal surface sealant (kulzer). For the in situ experiment, 10 volunteers wore an intraoral appliance containing eight specimens (two specimens per experimental group), with only one specimen from each experimental group being subjected to the acid process.
Influences of multi-pass friction stir alloying on characterization of AZ91D alloy-based dual reinforcement bio-ceramic nano-composites.
J Appl Biomater Funct Mater
January 2025
MOE Key Lab for Liquid-Solid Structure Evolution and Materials Processing, Shandong University, Jinan, China.
In current study, microstructural, mechanical and corrosion behaviour were investigated with incorporation of dual reinforced AZ91D surface composites. This research was carried out for enhancement of the bio-degradability in biological environment. The surface composites were successfully fabricated by friction stir processing method with a rotation speed of 800 rpm, travel speed of 80 mm/min and 2.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!