Study of a High-Temperature and High-Density Water-Based Drilling Fluid System Based on Non-sulfonated Plant Polymers.

The environment-friendly water-based drilling fluid system developed for the petroleum development industry cannot successfully withstand temperatures up to 180 °C, and most high temperature-resistant additives with sulfonic acid groups that have been successfully applied to water-based drilling fluid are not good for environmental protection. In order to solve the above technical problems, a non-sulfonated filtrate reducer and viscosity reducer with resistance to high temperature were prepared by using humic acid, lignin and a multifunctional monomer as raw materials. In laboratory experiments, the molecular weights of the FLO-H filtrate reducer and the VR-H viscosity reducer were 5.45 × 10 g/mol and 8.51 × 10 g/mol, respectively, and all of them showed good high-temperature resistance. The API filtration loss of the bentonite-base slurry with 3.0 wt% FLO-H was only 6.2 mL, which indicated that FLO-H had a prominent reduction in filtration loss after aging at high temperature. When the dosage of VR-H was 1.0 wt%, the plastic viscosity of the water-based drilling fluid after aging at 200 °C decreased from 71 mPa·s to 55 mPa·s, which provided excellent dispersion and dilution. The high-temperature and high-density water-based drilling fluid containing the FLO-H filtrate reducer and the VR-H viscosity reducer had good suspension stability and low filtration performance at the high temperature of 200 °C, which can meet the requirements of high-temperature deep well drilling.