Preparation and properties of nano silica-based bioactive glass/apatite/sodium alginate composite hydrogel.

In this paper, given the lack of osteogenic activity of sodium alginate (SA) hydrogel and to simulate the composition of natural bone, ionic-crosslinking NBG/n-HA/SA hydrogel scaffolds were prepared by using nano bioactive glass (NBG) and nano hydroxyapatite (n-HA) with high bioactivity as composite calcium sources and reinforcement phases, and D-gluconic acid δ-lactone (GDL) as the coagulant. The results showed that the mixture of the precursor forming the network had good injectability and plasticity. When the dosage of GDL was 0.75 g, the gelling time of the composite hydrogel could be regulated within 4-8 min, and the hydrogel had high compressive strength (170-220 kPa), as well. When the mass ratio of calcium source to SA was 1:1, the crosslinking network was relatively uniform with a considerable number of large pores around 40 μm in the structure. In the immersion experiment in vitro, it was found that the composite hydrogel could promote the deposition of bone-like apatite on the material's surface. Meanwhile, the cell experiments in vitro verified that the NBG/n-HA/SA composite hydrogel had good cytocompatibility without cytotoxicity. Moreover, the composite hydrogel could enhance the activity of ALP of mouse bone marrow mesenchymal stem cells, and thus, it had good osteogenic activity.