Polydopamine and Mercapto Functionalized 3D Carbon Nano-Material Hybrids Synergistically Modifying Aramid Fibers for Adhesion Improvement.

In order to solve the problem of poor interfacial adhesion between aramid fibers and a rubber matrix, an efficient and mild modification method was proposed via polydopamine and mercapto functionalized graphene oxide (GO) and carbon nanotube (CNTs) hybrids synergistically modifying aramid fibers. GO and CNTs were firstly stacked and assembled into unique 3D GO-CNTs hybrids through π-π conjugation. Then, the mercapto functionalization of the assembled 3D GO-CNTs hybrids was realized via the dehydration condensation reaction between the hydroxyls of GO and the silanol groups of coupling agent. Finally, the mercapto functionalized 3D GO-CNTs hybrids were grafted onto the aramid fibers, which were pre-modified by polydopamine through the Michael addition reaction mechanism. The surface morphology and chemical structures of GO-CNTs hybrids and fibers and the interfacial adhesion strength between fibers and rubber matrix were investigated. The results showed that the modification method had brought about great changes in the surface structure of fibers but not generated any damage traces. More importantly, this modification method could improve the interfacial strength by 110.95%, and the reason was not only the reactivity of functional groups but also that the 3D GO-CNTs hybrids with excellent mechanical properties could effectively share interfacial stress. The method proposed in this paper was universal and had the potential to be applied to other high-performance fiber-reinforced composites.