Single-step salt-template-based scalable production of 2D carbon sheets heterostructured with nickel nanocatalysts for lowering overpotential of hydrogen evolution reaction.

Non-precious metals have been considered as suitable alternatives for high-performance hydrogen evolution reactions (HER). Although the incorporation of carbon substances is shown to improve the number of active sites, electron transfer pathways, and long-term stability, there have been rare reports on their single-step scalable production. Herein, we realize free-standing two-dimensional (2D) carbon sheets heterostructured with nickel (Ni) nanocatalysts by pyrolyzing ultrathin layers of acetate tetrahydrate (i.e. the single precursor for both Ni and C sources) over water-soluble salt crystals. Such a salt-templated methodology is environmentally friendly and readily scalable without the implementation of sophisticated equipment. The resulting 2D carbon sheets exhibit an average small thickness of ∼ 3 nm and lateral dimensions with tens of micrometers, where a large number of nano-sized Ni particles with an average diameter of 14 nm are uniformly dispersed. Such 2D Ni-C sheets demonstrate a small overpotential of 111 mV at 10 mA/cm and a low Tafel slope of 86 mV/dec for HER in 1 M KOH, which is significantly improved over those of reported non-precious metals composited with carbon substances. This work offers new insight into the design and practical production of non-precious metal matrixes for economical HER.