Effect of thermocycling on the mechanical properties, inorganic particle release and low temperature degradation of glazed high translucent monolithic 3Y-TZP dental restorations.

The influence of thermocycling on the surface deterioration of glazed monolithic high translucent 3Y-TZP dental restorations is still unclear. The purpose of this study therefore was to evaluate low temperature degradation (LTD), elemental release and surface degradation pattern after five years of simulated clinical time. A total of 123 specimens were prepared from second-generation high translucent 3Y-TZP as per ISO 6872:2015 standards (3 mm × 4 mm × 30 mm). They were classified as per glazing and thermocycling protocol; group CPT, DGT and IGT. Glaze materials were applied on one surface of the specimen and subjected to a thermocycling in artificial saliva, four-point bending test, inductively coupled plasma mass spectrometry (ICP-MS), scanning electron microscopy (SEM), energy dispersive x-ray spectroscopy (EDX) and x-ray diffraction (XRD). Flexural strength, characteristic strength and Weibull modulus values were derived from four-point bending test. Descriptive fractographic analysis of surfaces was conducted to observe the surface degradation characteristics and point of failure. Control/no glaze with thermocycling (CPT = 621.5, 1σ = 117.0 MPa) presented higher flexural strength values compared to glaze I with thermocycling (442.4, 1σ = 45.4 MPa) and glaze II with thermocycling (534.3, 1σ = 46.3 MPa). Characteristic strength from Weibull analysis also observed higher values (669.2 MPa) for the control specimens. XRD analysis showed that monoclinic volume fraction (V = 11.0, 1σ = 0.7%) was highest in control specimens. Fractographic analysis suggested that there was no correlation between the point of failure initiation and mean flexural strength values. Glazing protected the high translucent 3Y-TZP surface against LTD during thermocycling but negatively impacted on the flexural strength.