The effect of prolonged holding time on the mechanical property and microstructural property of lithium disilicate glass-ceramic.

Repeat firing produces uncertainty about stabilizing lithium disilicate glass-ceramic (LDGC) material properties, even though prolonged holding time can enhance the mechanical property of LDGC during a single firing cycle. However, the effect of prolonged holding time and repeat firing on the mechanical property and microstructure of LDGC is not fully understood. In the present study, three groups of LDGC material were created: (i) extension of holding time (7 vs. 14 vs. 28 min) at 780-800 °C; (ii) holding time extension (7 vs. 14 min) and dual sintering at 800-820 °C, respectively; (iii) dual sintering with prolonged holding time (7 vs. 14 min) at 820-840 °C. The nano-indenter test revealed that prolonged holding time (14 and 28 min) promoted the enhancement of LDGC hardness and Young's modulus. X-ray photoelectron spectroscopy, X-ray diffraction and Fourier transform infrared spectroscopy confirmed that prolonged holding time increased and stabilized LD phase in LDGC, as well as induced residual compressive stress. Scanning electron microscopy showed that prolonged holding time increased LD crystal grains homogeneously and facilitated LDGC to form dense interlocking structure without enlarging crystal size grains significantly. In contrast, LDGC that dual sintered alone at 820-840 °C possessed inferior mechanical properties, coupled with heterogeneous crystal phases, residual tensile stress, and melted crystals grains in the porous microstructure. Interestingly, these deteriorated properties of LDGC caused by dual sintering alone could be counteracted by prolonging the holding time. Nevertheless, the LDGC materials displayed an excellent biocompatibility throughout the study. This study identified that prolonged holding time during repeated firing cycles stabilized LD phase and crystal grain size of LDGC, thus enhanced the mechanical properties, which provided a new insight to extend the repeat fired restoration longevity of LDGC. Graphical abstract.