Exceptional removal and immobilization of selenium species by bimetal-organic frameworks.

Binary metallic organic frameworks can always play excellent functions for pollutants removal. One binary MOFs, UiO-66(Fe/Zr)), was newly synthesized and applied to remove aquatic selenite (SeIV) and selenate (SeVI). The adsorption behaviors and mechanisms were investigated using batch experiments, spectroscopic analyses, and theoretical calculations (DFT). The characterization results showed that the material inherited the topological structure of UiO-66 and excellent thermal stability. The large specific surface area (467.52 m/g) and uniform mesoporous structures of the synthesized MOFs resulted in fast adsorption efficiency and high adsorption capacity for selenium species. The adsorbent kept high adsorption efficiency in a wide pH range from 2 to 11 with good anti-interference ability. The maximum adsorption capacity for Se(IV) and Se(VI) reached as high as 196 mg/g at pH 3 and 258 mg/g at pH 5, respectively. The process was conformed to fit pseudo-second-order kinetics and Langmuir isotherm, and could be explained by the formation of Fe/Zr-O-Se bond on the material surface, which was interpreted by the results of XPS, FTIR and DFT calculation. The regeneration and TCLP experiments demonstrated that UiO-66(Fe/Zr) could be regenerated for five cycles without obvious decrease of efficiencies, and the leaching rate of the adsorbed Se(IV) and Se(VI) in the spent adsorbent were only 4.8% and 2.3%. More than 99% of original Se(IV) and Se(VI) in the lake and tap water samples (1.0 mg/L of Se) could be removed in 2.0 h.