Effect of the Preparation Conditions on the Catalytic Properties of CoPt for Highly Efficient 4-Nitrophenol Reduction.

CoPt alloys with Pt contents from 15 to 90% were prepared using low-cost electrochemical deposition. Different samples were synthesized from electrochemical baths at pH = 2.5 and 5.5 in a solution with and without saccharin as an additive. The morphology, composition and crystalline structure of the as-prepared samples were investigated by High Resolution-Scanning Electron Microscopy (HR-SEM), Atomic Force Microscopy (AFM), Ultra-high Resolution-Transmission Electron Microscopy (UHR-TEM), Energy-Dispersive X-ray Spectroscopy (EDX), and X-ray Diffraction (XRD). XRD investigations revealed that fcc crystalline structure transforms into hcp crystalline structure when the pH of the electrochemical bath is increased from 2.5 to 5.5 as well as when saccharin is added to the electrochemical bath. The catalytic performance of the CoPt alloys for the nitro to amino phenol compounds conversion was investigated for all the prepared samples, and the results show that the conversion degree increases (from 11.4 to 96.5%) even though the Pt content in the samples decreases. From the samples prepared from the electrochemical bath with saccharin, a study regarding the effect of contact time was performed. The results indicated that after only 5 min, the CoPt sample prepared at pH = 5.5 in the presence of saccharin completely converted the nitro compound to an amino compound.