Objectives: Implant-supported restorations are generally used for the replacement of the lost teeth. Stability against masticatory forces and proper retention are critical for optimal durability of restorations. The aim of this experimental study was to compare the retention of cobalt-chromium (Co-Cr) copings made by different techniques.
Materials And Methods: Twenty-four solid abutment analogs were mounted and scanned with a desktop scanner. They were divided into two groups (n=12) and received metal copings fabricated by either soft or hard Co-Cr alloy. Soft Ceramill Sintron Co-Cr patterns were milled and sintered. Hard Co-Cr blocks were milled in a milling machine. The copings were sandblasted, polished, adjusted, and placed on the respective abutments. The frequency of adjustments was recorded for each abutment. The copings were cemented with zinc phosphate cement and underwent tensile test by a universal testing machine. The Mann-Whitney test and t-test were used to compare the two groups (α=0.05).
Results: There was no significant difference in retention of copings between the experimental groups. The mean retentive force was 559.58±115.66 N and 557.13 ±130.48 N for the soft and hard metal groups, respectively (P=0.96). Considering the non-normal distribution of adjustment frequency data, the Mann-Whitney test showed that the frequency of adjustments was significantly higher in the hard metal group than the soft metal group (9.5 versus 0.1667; P<0.001).
Conclusion: Although hard metal copings required more adjustments, retention of soft and hard Co-Cr copings was not significantly different.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC9375120 | PMC |
| http://dx.doi.org/10.18502/fid.v17i26.4652 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Ferrites with a Minimized Secondary Electron Yield.
Adv Sci (Weinh)
January 2025
School of Science and Engineering, University of Dundee, Nethergate, Dundee, DD1 4HN, UK.
Ferrites are an essential material in modern industry due to their exceptional magnetic properties and high resistivity. Many applications of ferrites necessitate exposure to high energy electrons, particularly space science and particle accelerators, where charging, multipacting, and electron clouds (ECs) are major issues. ECs are of particular concern around the Ni/Zn soft ferrite kicker magnets as the large hadron collider (LHC) undergoes its high luminosity upgrade.
View Article and Find Full Text PDFHighly Conductive, Ultratough, and Adhesive Eutectogels with Environmental Tolerance Enabled by Liquid Metal Composites.
Small
January 2025
School of Materials Science and Engineering, Suzhou University of Science and Technology, Suzhou, 215009, China.
Eutectogels are recently emerged as promising alternatives to hydrogels owing to their good environmental stability derived from deep eutectic solvents (DES). However, construction of competent eutectogels with both high conductivity and mechanical toughness is still difficult to achieve yet highly demanded. In this work, new LMNP-PEDOT-CMC-AA (LPCA) eutectogels are prepared using acrylic acid (AA) and carboxymethylcellulose sodium (CMC) as polymeric networks, liquid metal nanoparticle-poly(3,4-ethylenedioxythiophene) (LMNP-PEDOT) are added as multifunctional soft fillers.
View Article and Find Full Text PDFA compliant metastructure design with reconfigurability up to six degrees of freedom.
Nat Commun
January 2025
Morphing Matter Lab, Human-Computer Interaction Institute, Carnegie Mellon University, Pittsburgh, PA, USA.
Compliant mechanisms with reconfigurable degrees of freedom are gaining attention in the development of kinesthetic haptic devices, robotic systems, and mechanical metamaterials. However, available devices exhibit limited programmability and form-customizability, restricting their versatility. To address this gap, we propose a metastructure concept featuring reconfigurable motional freedom and tunable stiffness, adaptable to various form factors and applications.
View Article and Find Full Text PDFGel polymer electrolytes based on sulfonamide functional polymer nanoparticles for sodium metal batteries.
Phys Chem Chem Phys
January 2025
Institute for Frontier Materials, Deakin University, Geelong, Victoria 3216, Australia.
In this work, we investigate the development of polymer electrolytes for sodium batteries based on sulfonamide functional polymer nanoparticles (NaNPs). The synthesis of the polymer NaNPs is carried out by emulsion copolymerization of methyl methacrylate and sodium sulfonamide methacrylate in the presence of a crosslinker, resulting in particle sizes of 50 nm, as shown by electron microscopy. Then, gel polymer electrolytes are prepared by mixing polymer NPs and different organic plasticizers including carbonates, glymes, sulfolanes and ionic liquids.
View Article and Find Full Text PDFPeri-implant soft tissue conditioning of immediate posterior implants by CAD-CAM socket sealing abutments: a randomized clinical trial.
BMC Oral Health
January 2025
Department of Fixed Prosthodontics, Faculty of Dentistry, Cairo University, Cairo, Egypt.
Background: Anatomically formed healing abutments were suggested in literature to address many of the issues associated with immediate posterior implant insertion such as large extraction sockets that are extremely hard to seal without reflecting the mucoperiosteal flap, extraction sockets anatomy that are not suitable for regular healing abutment placement, and potentially high occlusal stresses when planning a temporary implant supported prothesis to improve the conditioning of supra implant tissue architecture and the emergence profile of the implant supported restorations.
Purpose: To clinically evaluate the peri-implant soft tissue profile of single posterior implant retained restorations and to assess patient related outcomes of the implant restorations that were conditioned immediately by CAD-CAM socket sealing abutments (SSA) versus those conditioned by Titanium (Ti) standard healing abutments (SHA).
Methods: Twenty participants received twenty-two single maxillary immediate implants after flapless minimally invasive tooth extraction and 3D guided implant placement in the posterior area (premolar and molar) and allocated randomly into two groups (n = 11), the intervention group: patients received PEEK SSA and the control group: the patients received Ti SHA.
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!