To investigate shear bond strength (SBS) of three restorative materials on primary dentin after silver diamine fluoride (SDF) application.
Thirty primary teeth were randomized into three groups of 10 teeth. Each tooth was split mesiodistally and randomized into experimental (artificial caries plus SDF) and control (sound dentine without SDF) groups. Glass ionomer cement (GIC), resin-modified bioactive resin (ACTIVA), and composite resin (CR) restorations were tested for SBS and mode of failure (MF).
All SDF groups exhibited significantly lower SBS compared to the control (CR: =0.001; ACTIVA: =0.001; GIC: =0.004). For the SDF group, the compa- rison of materials was statistically significant ( =0.006); posthoc tests showed significance only between CR and ACTIVA ( =0.009) and between ACTIVA and GIC ( =0.020). The lowest mean value was obtained for ACTIVA (1.4 MPa) and the highest mean value was obtained for CR (3.3 MPa). For the control group, Welch's F test was statistically significant ( =0.044), but all posthoc tests were not. For MF, SDF exhibited a significantly greater percentage of adhesive failures with ACTIVA and CR than with GIC. In the control group, a mixed MF was more dominant with no significant differences.
The SDF group had significantly lower SBS.
Download full-text PDF |
Source |
|---|
Publication Analysis
Top Keywords
Similar Publications
Shear bond strength and ARI scores of metal brackets to glazed glass ceramics and zirconia: an in vitro study investigating surface treatment protocols.
BMC Oral Health
December 2024
Faculty of Dentistry, Innovative Dental Materials and Interfaces Research Unit (URB2i), UR 4462, Paris Cité University, 1 rue Maurice Arnoux, Montrouge, 92120, France.
Objective: To evaluate the shear bond strength (SBS) and adhesive remnant index (ARI) scores of metal brackets to glazed lithium disilicate reinforced glass-ceramics and zirconia according to various surface treatment protocols.
Methods: A total of 240 lithium disilicate ceramic (LD) and 240 zirconia (Zr) blocks were randomly divided according to sandblasting, hydrofluoric acid (HF) etching, universal primer use, and the adhesive system applied. A maxillary canine metal bracket was bonded to each sample with resin cement (Transbond XT, TXT).
Evaluation of the Effect of Chitosan-Based Irrigation Solutions on the Bond Strength of Mineral Trioxide Aggregate to Bulk-Fill Composite.
J Funct Biomater
December 2024
Department of Endodontics, Faculty of Dentistry, Gazi University, 06490 Ankara, Türkiye.
Bond strength between repair and restorative materials is crucial for endodontic success. This study assessed the effects of the following final irrigation solutions on the bond strength of mineral trioxide aggregate (MTA) to a bulk-fill composite: (1) 17% Ethylenediamine tetraacetic acid (EDTA); (2) 2% Chlorhexidine (CHX); (3) 0.2% chitosan; (4) 0.
View Article and Find Full Text PDFEffect of Mechanical Surface Treatment on Shear Bond Strength of Orthodontic Brackets to 3D Printed and Milled CAD/CAM Provisional Materials: An In Vitro Study.
J Funct Biomater
November 2024
King Abdullah International Medical Research Center, Riyadh 11481, Saudi Arabia.
The aim of the study is to assess the impact of mechanical surface treatments on the shear bond strength (SBS) of orthodontic brackets bonded to three-dimensional (3D) printed and milled CAD/CAM provisional materials. Sixty cylindrical samples were fabricated for each provisional material. Samples were treated with one of the following surface treatments: aluminum oxide airborne particle abrasion, diamond bur rotary instrument roughening, and phosphoric acid etching (control).
View Article and Find Full Text PDFEvaluation of Shear Bond Strength of Lithium Disilicate Veneers Using Pre-heated Resin Composite With Two Conventional Resin Cements: An In Vitro Study.
Cureus
November 2024
Department of Endodontic and Operative Dentistry, Damascus University, Damascus, SYR.
Objectives This study aimed to compare the shear bond strength of three resin cements (light-cured resin cement, pre-heated composite resin, and dual-cured self-adhesive resin cement) when bonding to lithium disilicate discs. Materials and methods Thirty-six discs made of lithium disilicate were fabricated and etched with 9.5% (HF), and 36 human premolars were collected and immersed in the acrylic molds, then randomly divided into three equal groups (n = 12): Group 1: light-cured resin cement, Group 2: pre-heated resin composite, and Group 3: dual-cured resin cement.
View Article and Find Full Text PDFEvaluation of the shear bond strength of surface-treated Cobalt-Chromium metal crowns on corticobasal® implant abutments cemented using different luting agents.
J Stomatol Oral Maxillofac Surg
December 2024
Reader, Department of Periodontics, Saveetha Dental College and Hospitals, Saveetha Institute of Medical and Technical Sciences, Saveetha University, Chennai 600077, Tamil Nadu, India.. Electronic address:
Purpose: This in-vitro study aimed to compare the shear bond strength (SBS) of cobalt-chromium (Co-Cr) crowns on Corticobasal® implant abutments, evaluating the effects of two surface treatments and two luting agents.
Materials And Methods: Thirty Co-Cr crowns were fabricated using CAD-CAM technology with a direct metal laser sintering process and divided into three groups based on surface treatment: Group I (untreated), Group II (sandblasted with 50 μm Al₂O₃), and Group III (Er: YAG laser etching). Each group was further subdivided based on luting cement: Sub group A (GC Fuji Plus) and Sub group B (Rely X U200).
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!