Valorizing hazardous lead glass sludge and alumina flakes filling waste for the synthesis of geopolymer building bricks.

Geopolymer bricks from lead glass sludge (LGS) and alumina flakes filling (AFF) waste were synthesized in the present work. AFF waste was chemically treated to prepare sodium aluminate (NaAlO) powder. Silicate source (untreated LGS and thermally treated one at 600 °C (LGS600)) and sodium oxide (NaO) concentration (as NaAlO) were the compositional parameters, which affected the physical and mechanical properties (compressive strength, water absorption, and bulk density) of the prepared bricks. High organic matter content inside LGS caused a retardation effect on the geopolymerization process, resulting in the formation of hardened bricks with modest 90-day compressive strengths (2.13 to 4.4 MPa). Using LGS600 enhanced the mechanical properties of the fabricated bricks, achieving a maximum 90-day compressive strength of 22.35 MPa at 3 wt.% NaO. Sodium aluminosilicate hydrate was the main activation product inside all samples, as confirmed by X-ray diffraction and thermal analyses. Acetic acid leaching test also proved that all LGS600-NaAlO mixtures represented Pb concentrations in leachates lower than the permissible level of characteristic leaching procedures, indicating the mitigation of environmental problems caused by these wastes.