Concentration-Driven Self-Assembly of PS--PLA Bottlebrush Diblock Copolymers in Solution.

Bottlebrush polymers are a class of semiflexible, hierarchical macromolecules with unique potential for shape-, architecture-, and composition-based structure-property design. It is now well-established that in dilute to semidilute solution, bottlebrush homopolymers adopt a wormlike conformation, which decreases in extension (persistence length) as the concentration and molecular overlap increase. By comparison, the solution phase self-assembly of bottlebrush diblock copolymers (BBCP) in a good solvent remains poorly understood, despite critical relevance for solution processing of ordered phases and photonic crystals. In this work, we combine small-angle X-ray scattering, coarse-grained simulation, and polymer synthesis to map the equilibrium phase behavior and conformation of a set of large, nearly symmetric PS--PLA bottlebrush diblock copolymers in toluene. Three BBCP are synthesized, with side chains of number-averaged molecular weights of 4500 (PS) and 4200 g/mol (PLA) and total backbone degrees of polymerization of 100, 255, and 400 repeat units. The grafting density is one side chain per backbone repeat unit. With increasing concentration in solution, all three polymers progress through a similar structural transition: from dispersed, wormlike chains with concentration-dependent (decreasing) extension, through the onset of disordered PS/PLA compositional fluctuations, to the formation of a long-range ordered lamellar phase. With increasing concentration in the microphase-separated regimes, the domain spacing increases as individual chains partially re-extend due to block immiscibility. Increases in the backbone degree of polymerization lead to changes in the scattering profiles which are consistent with the increased segregation strength. Coarse-grained simulations using an implicit side-chain model are performed, and concentration-dependent self-assembly behavior is qualitatively matched to experiments. Finally, using the polymer with the largest backbone length, we demonstrate that lamellar phases develop a well-defined photonic band gap in solution, which can be tuned across the visible spectrum by varying polymer concentration.