Formation and Detection of High-Pressure Oxygen in Closed Pores of LaSrCoO Solid Oxide Electrolysis Anodes.

The chemical capacitance of LaSrCoO (LSC) thin film microelectrodes with different microstructures was investigated upon varying anodic DC voltages. Dense and porous electrodes (open porosity) were prepared by using different parameters during pulsed laser deposition (PLD). Furthermore, electrodes with closed porosity were fabricated by depositing a dense capping layer on a porous film. Electrochemical impedance spectroscopy (EIS) was performed in synthetic air at 460 and 608 °C with anodic DC voltages up to 440 mV. Chemical capacitance values of the electrodes were derived from the obtained spectra. While the chemical capacitance of dense and porous electrodes decreased as expected with increasing anodic overpotential, electrodes with closed pores exhibited very unusual peaks with extremely high values of >8000 F/cm at overpotentials of >100 mV. We demonstrate that this huge capacitance increase agrees very well with calculated chemical capacitances deduced from a real gas equation. Hence, we conclude that the formation of highly pressurized oxygen (up to gas pressures of ∼10 bar) in closed pores is responsible for this strong capacitive effect at anodic overpotentials. Such measurements can thus detect and quantify the buildup of high internal gas pressures in closed pores at the anode side of solid oxide electrolysis cells.