AI Article Synopsis
Article Abstract
Purpose: This analysis aimed to evaluate the intaglio surface trueness, antagonist's wear volume loss, and fracture resistance of full-contour crowns of (Y, Nb)-stabilized fully-sintered zirconia (FSZ), 4 mol% or 5 mol% yttria-stabilized partially sintered zirconia (4YZ or 5YZ) with high-speed sintering.
Materials And Methods: A total of 42 zirconia crowns were separated into three groups: FSZ, 4YZ, and 5YZ (n = 14). The intaglio surface trueness of the crowns was evaluated at the inner surface, occlusal, margin, and axial areas and reported as root-mean-square, positive and negative average deviation. Half of the specimens were aged for 120,000 cycles in the chewing simulator, and the wear volume loss of antagonist was measured. Before and after chewing, the fracture load was measured for each group. The trueness values were analyzed with Welch's ANOVA, and the wear volume loss with the Kruskal-Wallis tests. Effect of the zirconia type and aging on fracture resistance of crowns was tested using two-way ANOVA.
Results: The intaglio surface trueness measured at four different areas of the crown was less than 50 µm, regardless of the type of zirconia. No significant in wear volume loss of antagonists were detected among the groups ( > .05). Both the type of zirconia and aging showed statistically significant effects on fracture resistance ( < .05).
Conclusion: The full-contour crowns of FSZ as well as 4YZ or 5YZ with high-speed sintering were clinically acceptable, in terms of intaglio surface trueness, antagonist's wear volume loss, and fracture resistance after simulated mastication.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC9259349 | PMC |
| http://dx.doi.org/10.4047/jap.2022.14.3.173 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Biocompatible TA4 and TC4ELI with excellent mechanical properties and corrosion resistance via multiple ECAP.
Biomed Mater
December 2024
State Key Laboratory of Nuclear Physics and Technology, Department of Technical Physics, School of Physics, Peking University, Beijing 100871, People's Republic of China.
Titanium (Ti), characterized by its exceptional mechanical properties, commendable corrosion resistance and biocompatibility, has emerged as the principal functional materials for implants in biomedical and clinical applications. However, the Ti-6Al-4V (TC4ELI) alloy has cytotoxicity risks, whereas the strength of the existing industrially pure titanium TA4 is marginally inadequate and will significantly limit the scenarios of medical implants. Herein, we prepared ultrafine-grained industrial-grade pure titanium TA4 and titanium alloy TC4ELI via the equal channel angular pressing method, in which the TA4-1 sample has ultrahigh strength of 1.
View Article and Find Full Text PDFWear resistance of 3D printed, milled, and prefabricated methacrylate-based resin materials: An in vitro study.
J Prosthet Dent
December 2024
Assistant Professor, Department of Prosthodontics, Faculty of Dentistry, Chiang Mai University, Chiang Mai, Thailand. Electronic address:
Statement Of Problem: Three-dimensional (3D) printing and milling technologies have been increasingly used in prosthodontic practice for fabricating digital prostheses. Nevertheless, evidence relating to the wear resistance of denture teeth fabricated using these methods is lacking.
Purpose: The purpose of this in vitro study was to compare the wear resistance exhibited by denture teeth fabricated using 3D printing and milling technologies with prefabricated denture teeth.
Perspective of Tribological Mechanisms for α-Alkene Molecules with Different Chain Lengths from Interface Behavior.
Langmuir
December 2024
State Key Laboratory of Fluorinated Functional Membrane Materials, Dongyue Fluorosilicone Technology Group, Zibo 256400, China.
Three α-alkene lubricants, differentiated by chain length, were selected as model compounds to investigate the influence of chain length on tribological properties. The novelty of this study lies in setting chain length as the sole variable to explore its impact on surface and adsorption energy. Based on the above findings, the study provides a unique explanation of the intrinsic relationship between chain length and tribological performance.
View Article and Find Full Text PDFEnhanced Wear Resistance and Thermal Dissipation of Copper-Graphene Composite Coatings via Pulsed Electrodeposition for Circuit Breaker Applications.
Materials (Basel)
December 2024
Department of Enterprise Engineering "Mario Lucertini", University of Rome Tor Vergata, 00133 Rome, Italy.
Copper, though highly conductive, requires improved wear resistance and thermal dissipation in applications that involve continuous movement and current-induced vibrations, such as power breakers. Conventional solutions, such as copper-tungsten alloys or lubricant use, face limitations in durability, friction, or environmental impact. This study explores the development of copper-graphene (Cu-GNPs) composite coatings using pulsed electrodeposition to enhance the tribological, thermal, and mechanical properties of circuit breaker components by adopting an industrially scalable technique.
View Article and Find Full Text PDFEffect of Ball Burnishing on Fretting at Elevated Temperatures.
Materials (Basel)
December 2024
Faculty of Mechanical Engineering and Aeronautics, Rzeszow University of Technology, Powstancow Warszawy 8 Street, 35-959 Rzeszow, Poland.
The influence of ball burnishing on friction and wear at elevated temperatures under fretting conditions has not yet been reported. Fretting experiments were conducted using the Optimol SRV5 tester (Optimol Instruments, Munich, Germany) under dry gross fretting conditions. A ball of WC ceramic was pressed against a disc from the titanium alloy Ti6Al4V.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!