Enrichment of biogas through composite membrane of PEBA-1657/ hierarchical T-type zeolite.

Presently, composite membranes emerged as a promising approach to overcome the limitations of polymeric and inorganic membranes particularly in acid gas separation. In the present work, composites membranes were fabricated by combining hierarchical T-Type (h-zeolite T) zeolite and PEBA-1657 at different filler composition that ranging from 5 wt% - 30 wt% for the CO/CH separation. The physicochemical properties of the resultant inorganic filler and membranes were investigated by using Brunauer-Emmett- Teller (BET), field emission scanning electron microscopy (FESEM), Fourier Transform infra-red (FTIR), x-ray diffraction (XRD), thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). FESEM and EDX analysis revealed that the formation of voids and agglomeration of particles is pronounced as the fillers loading was increased up to 30 wt%. The single gas permeation test demonstrated that amalgamation of h-zeolite T particles into PEBA-1657 has resulted in the improvement of CO permeability up to 122% and CO/CH selectivity up to 31%. Hybrid membrane encapsulated with 25 wt% of h-zeolite T displayed a maximum separation efficiency with the highest CO permeability of 164.83 Barrer and CO/CH selectivity of 19.37. However, further increment of fillers composition up to 30 wt% resulted in a sharp reduction of COCH selectivity to 15.80 due to the particles sedimentation and agglomeration. Overall, the favorable gas transport behavior of PEBA-1657/h-zeolite T composite membrane indicates its promising prospect for CO/CH separation especially in biogas and natural gas purification application. Future research efforts are directed on the optimization of the fabrication parameters and performance investigation at different operating condition to further enhance the CO separation and extend its operability under various environment.