An eco-friendly and sustainable support of agave-fibers functionalized with graphene/TiO2:SnO2 for the photocatalytic degradation of the 2,4-D herbicide from the drinking water.

In this research, we evaluated the photocatalytic performance of biodegradable composites for the removal of the 2,4-Dichlorophenoxyacetic acid (2,4-D) herbicide. The composite was composed by agave fibers (AgF), graphene-microplates (GM) and titanium dioxide TiO/SnO (TSn) nanoparticles (NPs) and was named TSn + AgF/GM. Both, the TSn NPs and the GM were deposited on the AgF using the Dip-coating method. According to the analysis by X-Ray Diffraction (XRD), the crystalline phase for the TiO and SnO was anatase and tetragonal-rutile, respectively. The Scanning Electron Microscopy (SEM) images demonstrated that the AgF were completely saturated by the GM (which had average dimensions of 15 μm × 22 μm) and by conglomerations of TSn NPs with average size of 642 nm. The TSn NPs and the TSn + AgF/GM composite were evaluated for the photocatalytic degradation of the 2,4-D herbicide under ultraviolet-visible (UV-Vis) light and found a maximum degradation of 98.4 and 93.7% (after 4 h) for the TSn NPs and the TSn + AgF/GM composite, respectively. Reuse cycles were also performed and the degradation percentage decreased by 13.1% and by 7.8% (after 3 cycles of reuse) when the TSn NPs and the TSn + AgF/GM composite are employed, respectively. Scavenger experiments were also carried out and found that the oxidizing agents are mainly produced in the order of: •OH>•O > h; then, the main oxidizing agents generated during the photocatalytic reaction were the hydroxyl radicals. Thus, the photocatalytic system studied in this work for the degradation of 2,4-D could pave the way for the development of new eco-friendly/floatable photocatalysts, which can be applied in wastewater-treatment plants.