Purpose: To investigate the influence of primers on polymerization kinetics of resin-based luting and its effect on the microhardness and bond strength to zirconia. Materials and Methods: Panavia V5 (PV; Kuraray Noritake) with Tooth Primer (TPprimer; Kuraray Noritake) or Clearfil Ceramic Primer (CPprimer; Kuraray Noritake), and RelyX Ultimate (RU; 3M Oral Care) with Scotchbond Universal (SUadhesive; 3M Oral Care) were evaluated. Polymerization kinetics of luting materials with or without primers (TPprimer or SUadhesive) were evaluated using Fourier transform near-infrared (FT-NIR) spectroscopy in self- and dual-curing modes (n = 5). Microhardness of luting materials was evaluated after 1, 12, and 24 h (n = 5). Shear bond strengths to zirconia ceramics (Katana Zirconia, Kuraray Noritake; and Lava Esthetic, 3M Oral Care) after 24 h and 1 year (n = 8) were assessed to determine the effect of the following surface treatments: no treatment, non-thermal atmospheric plasma, primer (CPprimer or SUadhesive), and the combination of plasma + primers. Statistical analyses were performed at a 5% significance level.
Results: PV achieved a significantly higher degree of conversion (DC) when TPprimer was used, while there was no increase in conversion for RU combined with SUadhesive. Light activation significantly improved polymerization, which also produced greater microhardness. CPprimer and SUadhesive significantly improved immediate bond strength to zirconia ceramics. However, after 1 year, only SUadhesive with RU was able to maintain the bond strength. Plasma surface treatment did not improve bonding to zirconia.
Conclusion: The use of primers improved the DC for PV only. Light curing produced higher conversion and microhardness for both resin-based luting materials. Bond strength to zirconia was improved when primers were used. However, only RU demonstrated reliable long-term adhesion to zirconia.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.3290/j.jad.b3146833 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Shear bond strength and ARI scores of metal brackets to glazed glass ceramics and zirconia: an in vitro study investigating surface treatment protocols.
BMC Oral Health
December 2024
Faculty of Dentistry, Innovative Dental Materials and Interfaces Research Unit (URB2i), UR 4462, Paris Cité University, 1 rue Maurice Arnoux, Montrouge, 92120, France.
Objective: To evaluate the shear bond strength (SBS) and adhesive remnant index (ARI) scores of metal brackets to glazed lithium disilicate reinforced glass-ceramics and zirconia according to various surface treatment protocols.
Methods: A total of 240 lithium disilicate ceramic (LD) and 240 zirconia (Zr) blocks were randomly divided according to sandblasting, hydrofluoric acid (HF) etching, universal primer use, and the adhesive system applied. A maxillary canine metal bracket was bonded to each sample with resin cement (Transbond XT, TXT).
Long-Term Dentin Bonding Performance of Universal Adhesives: The Effect of HEMA Content and Bioactive Resin Composite.
J Funct Biomater
December 2024
Department of Restorative Dentistry, Graduate School of Dental Medicine, Hokkaido University, Sapporo 060-8586, Japan.
This study investigated the effects of resin composites (RCs) containing surface pre-reacted glass ionomer (S-PRG) filler on the dentin microtensile bond strength (μTBS) of HEMA-free and HEMA-containing universal adhesives (UAs). Water sorption (WS) and solubility (SL), degree of conversion (DC), and ion release were measured. The UAs BeautiBond Xtreme (BBX; 0% HEMA), Modified Adhesive-1 (E-BBX1; 5% HEMA), Modified Adhesive-2 (E-BBX2; 10% HEMA), and two 2-step self-etch adhesives (2-SEAs): FL-BOND II (FBII; with S-PRG filler) and silica-containing adhesive (E-FBII) were used.
View Article and Find Full Text PDFEvaluation of the Effect of Chitosan-Based Irrigation Solutions on the Bond Strength of Mineral Trioxide Aggregate to Bulk-Fill Composite.
J Funct Biomater
December 2024
Department of Endodontics, Faculty of Dentistry, Gazi University, 06490 Ankara, Türkiye.
Bond strength between repair and restorative materials is crucial for endodontic success. This study assessed the effects of the following final irrigation solutions on the bond strength of mineral trioxide aggregate (MTA) to a bulk-fill composite: (1) 17% Ethylenediamine tetraacetic acid (EDTA); (2) 2% Chlorhexidine (CHX); (3) 0.2% chitosan; (4) 0.
View Article and Find Full Text PDFEffect of Mechanical Surface Treatment on Shear Bond Strength of Orthodontic Brackets to 3D Printed and Milled CAD/CAM Provisional Materials: An In Vitro Study.
J Funct Biomater
November 2024
King Abdullah International Medical Research Center, Riyadh 11481, Saudi Arabia.
The aim of the study is to assess the impact of mechanical surface treatments on the shear bond strength (SBS) of orthodontic brackets bonded to three-dimensional (3D) printed and milled CAD/CAM provisional materials. Sixty cylindrical samples were fabricated for each provisional material. Samples were treated with one of the following surface treatments: aluminum oxide airborne particle abrasion, diamond bur rotary instrument roughening, and phosphoric acid etching (control).
View Article and Find Full Text PDFComparative Assessment of Push-Out Bond Strength and Dentinal Tubule Penetration of Different Calcium-Silicate-Based Endodontic Sealers.
Dent J (Basel)
December 2024
Faculty of Dentistry, Iuliu Hatieganu University of Medicine and Pharmacy, 400012 Cluj-Napoca, Romania.
Adhesion within endodontic obturation material and root canal walls improves the efficacy of the endodontic treatment by establishing a barrier that inhibits reinfection and entombs residual bacteria. This study evaluates the push-out bond strength (POBS) of calcium silicate sealers compared to an epoxy-resin-based sealer. A total of 36 extracted mono-radicular teeth were prepared with Pro Taper Ultimate and irrigated with 5.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!