Understanding Aging Mechanisms in the Context of UV Irradiation of a Low Fouling and Self-Cleaning PVDF-PVP-TiO Hollow-Fiber Membrane.

In the context of designing a photocatalytic self-cleaning/low-fouling membrane, the stability of PVDF-PVP-TiO hollow-fiber membranes under UV irradiation has been studied. The effect of irradiation power, aqueous environment composition and fouling state on the properties of the membranes has been investigated. With this aim, SEM observations, chemical analysis and tensile strength measurements have been conducted. The results indicate that pristine membranes that undergo UV irradiation in ultra-pure water are significantly degraded due to attacks of OH° radicals. However, when methylene blue, used as a model pollutant, is introduced in the aqueous environment, OH° radicals preferentially react with this molecule rather than the membranes, successfully preserving the original properties of the latter. The presence of an adsorbed BSA layer (pre-fouling by immersion) on the surface of the membrane delays membrane aging, as the BSA layer is degraded by radicals instead of the membrane material. The degradation of the BSA layer also validates the self-cleaning properties of the membrane. However, when membranes are pre-fouled by filtration of a 2 g/L BSA solution, delay to aging is less. This is because OH° radicals do not reach BSA molecules that are trapped inside the membrane pores, and therefore react with the membrane material.