This study aimed to evaluate the influence of calcium silicate-based sealers on the bond strength of fiber posts using conventional and self-adhesive resin cement. Sixty single-rooted teeth were selected. The canals were prepared with a reciprocating instrument 40.06. The roots were randomly distributed in six groups (n = 10) according to the strategies for root canal filling and fiber posts cementation: AH Plus/RelyX ARC; AH Plus/RelyX U200; Bio C Sealer/RelyX ARC; Bio C Sealer/RealyX U200; Sealer Plus BC/RelyX ARC; and Sealer Plus BC/RelyX U200. The roots were transversally sectioned, and one slice per post-third was obtained. The push-out test was performed at a crosshead speed of 1mm/min. The failure patterns were described after assessment with a stereomicroscope with a 10× magnification. Bond strength was calculated and analyzed using the ANOVA and Tukey test. AH Plus did not influence the bond strength of fiber posts cemented with conventional (RelyX ARC) or with self-adhesive resin cement (RelyX U200). The lowest bond strength values were obtained when calcium silicate-based sealers were associated with conventional resin cement (Bio C Sealer/RelyX ARC and Sealer Plus BC/RelyX ARC). Except for Sealer Plus BC/RelyX ARC, all groups presented lower bond strength at the apical portion compared to the cervical portion of the post. Adhesive failures between cement and post and cement and dentin were predominant (55.3%). Calcium silicate-based sealers decreased the bond strength of fiber posts cemented with conventional resin cement.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC9645158 | PMC |
| http://dx.doi.org/10.1590/0103-6440202204529 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Stereochemistry-Tuned Hydrogen-Bonding Synergistic Covalent Adaptable Networks: Towards Recycled Elastomers with Excellent Creep-Resistant Performance.
Angew Chem Int Ed Engl
January 2025
Sichuan University - Wangjiang Campus: Sichuan University, Polymer Research Institute, CHINA.
Covalent adaptable networks (CANs) offer innovative solutions for the reprocessing and recycling of thermoset polymers. However, achieving a balance between easy reprocessing and creep resistance remains a challenge. This study focuses on designing and synthesizing polyurethane (PU) materials with tailored properties by manipulating the stereochemistry of diamine chain extenders.
View Article and Find Full Text PDFEffect of sulfinate salt on bonding and polymerization of adhesive to intracoronally bleached dentin.
Sci Rep
January 2025
Department of Operative Dentistry, Faculty of Dentistry, Chulalongkorn University, 34 Henri Dunant Road, Pathumwan, Bangkok, 10330, Thailand.
To evaluate the effect of sulfinate salt on the bond performance of a two-step self-etch adhesive to an intracoronally bleached pulpal dentin surface. Intracoronally bleached bovine teeth were treated with or without sulfinate salt (sulfinate agent (SA): Clearfil DC activator) before 2-SEA (Clearfil SE Bond 2) application, while unbleached teeth served as the control (n = 5 teeth). Microtensile bond strength (µTBS) using the bonded surface area of 1 mm at the crosshead speed of 1 mm/min measurements after 24 h storage and thermocycles (TC), degree of conversion (DC) analyses by Raman spectroscopy (n = 3 teeth), ultrastructure of resin-dentin interface (n = 3 teeth), and intracoronally bleached pulp chamber dentin surface (n = 3 teeth) observations by scanning electron microscopy (SEM) were subsequently performed.
View Article and Find Full Text PDFHydrogen Evolution Reaction in Borophene: Puckering Mechanism and the Role of Coordination Number.
ACS Omega
January 2025
Department of New Energy Science and Engineering, Xiamen University Malaysia, Sepang 43900, Malaysia.
Using the free energy of hydrogen adsorption (Δ ) as the indicator, five borophene phases are previously shown to possess high catalytic activity for the hydrogen evolution reaction (HER). On these borophene phases, we investigate the role of the coordination number (CN = 4, 5, 6) of the adsorption sites and the puckering of the adsorption site. CN is discovered to have a profound effect on the Δ distribution, charge, and puckering height () of adsorption sites.
View Article and Find Full Text PDFPrimary Dentin Conditioning with Methylene Blue Activated Photodynamic Therapy, Phytic Acid, and Er,Cr:YSGG to Resin-Modified Glass Ionomer Cement in Comparison to Conventional Polyacrylic Acid.
Photobiomodul Photomed Laser Surg
January 2025
Department of Preventive Dental Sciences, College of Dentistry, Dar Al Uloom University, Riyadh, Saudi Arabia.
Impact of surface conditioner phytic acid (IP6) Er,Cr:YSGG laser (ECYL) methylene blue photodynamic therapy (MB-PDT) on the microleakage and shear bond strength (SBS) of resin-modified glass ionomer cement (RMGIC) to primary sound dentin. Overall, 80 extracted sound primary molars were collected followed by their submergence in self-cure acrylic resin. The dentin surface was exposed and made flat and was assigned into four groups based on the surface conditioning.
View Article and Find Full Text PDFBonding performance of universal adhesive systems with dual-polymerising resin cements to various dental substrates: in vitro study.
BMC Oral Health
January 2025
Department of Cariology and Operative Dentistry, Graduate School of Medical and Dental Sciences, Institute of Science Tokyo, 1-5-45 Yushima, Bunkyo-Ku, Tokyo, 113-8549, Japan.
Background: Resin cements often require substrate-specific pretreatment. Recently, universal adhesive systems have been introduced, simplifying procedures by eliminating the need for multiple adhesives and offering options that do not require light curing. This study investigated the bonding performance of universal adhesive systems combined with dual-polymerising resin cements on enamel, dentin, zirconia, lithium disilicate ceramics (LDS), and resin blocks.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!