High-Performance Surface-Enhanced Raman Scattering Substrates Based on the ZnO/Ag Core-Satellite Nanostructures.

Recently, hierarchical hybrid structures based on the combination of semiconductor micro/nanostructures and noble metal nanoparticles have become a hot research topic in the area of surface-enhanced Raman scattering (SERS). In this work, two core-satellite nanostructures of metal oxide/metal nanoparticles were successfully introduced into SERS substrates, assembling monodispersed small silver nanoparticles (Ag NPs) on large polydispersed ZnO nanospheres (p-ZnO NSs) or monodispersed ZnO nanospheres (m-ZnO NSs) core. The p-ZnO NSs and m-ZnO NSs were synthesized by the pyrolysis method without any template. The Ag NPs were prepared by the thermal evaporation method without any annealing process. An ultralow limit of detection (LOD) of 1 × 10 M was achieved in the two core-satellite nanostructures with Rhodamine 6G (R6G) as the probe molecule. Compared with the silicon (Si)/Ag NPs substrate, the two core-satellite nanostructures of Si/p-ZnO NSs/Ag NPs and Si/m-ZnO NSs/Ag NPs substrates have higher enhancement factors (EF) of 2.6 × 10 and 2.5 × 10 for R6G as the probe molecule due to the enhanced electromagnetic field. The two core-satellite nanostructures have great application potential in the low-cost massive production of large-area SERS substrates due to their excellent SERS effect and simple preparation process without any template.