Polytetrafluoroethylene (PTFE) and expanded PTFE (ePTFE) are ideal for various applications. Because PTFE does not flow, even when heated above its melting point, PTFE components are fabricated using a process called paste extrusion. This process entails blending PTFE powder particles with a lubricant to form PTFE paste, which is subsequently preformed, extruded, expanded (in the case of ePTFE), and sintered. In this study, ethanol was proposed as an alternative green lubricant for PTFE processing. Not only is ethanol benign and biofriendly, it provides excellent wettability and processing benefits. Using ethanol as a lubricant, the shear viscosity of PTFE paste and its flow behavior during paste extrusion were investigated. Frequency sweeps using a parallel-plate rheometer were performed on PTFE paste samples and various grits of sandpaper were used to reduce wall slip of PTFE paste. A viscosity model was generated and a multiphysics software was used to simulate PTFE paste extrusion. The simulated extrusion pressure was compared to experimental data of actual paste extrusion. Flow visualization experiments using colored PTFE layers were conducted to reveal the flow profile of the PTFE paste. The morphology of the expanded ePTFE tubes was examined using scanning electron microscopy and the effect of expansion ratio on ePTFE morphology was quantified.

Download full-text PDF

Source
http://www.ncbi.nlm.nih.gov/pmc/articles/PMC9017991PMC
http://dx.doi.org/10.1002/pen.25632DOI Listing

Publication Analysis

Top Keywords

ptfe paste
24
paste extrusion
20
ptfe
13
paste
10
extrusion
6
flow
5
viscosity characterization
4
characterization flow
4
flow simulation
4
simulation visualization
4

Similar Publications

Want AI Summaries of new PubMed Abstracts delivered to your In-box?

Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!