Achieving the potential multifunctional near-infrared materials CaIn Ga GeO:Cr using a solid state method.

Near-infrared spectroscopy is developing rapidly in the fields of human detection and food analysis due to its fast response and non-invasive characteristics. Herein, we report the novel near-infrared garnet-type CaInGeO:Cr and CaIn Ga GeO:0.07Cr phosphors, in which there are two crystallographic sites (CaO, InO) that can be substituted by Cr, and cation regulation engineering for In is utilized to tune the luminescence properties. Under the 480 nm excitation, the CaInGeO:Cr phosphor emits a broad spectrum at 650-1150 nm, which matches well with the first biological window. The concentration quenching mechanism and luminescence mechanism of CaInGeO:Cr were studied and the site assignment of the two luminescence centers was discussed using low temperature spectra and fluorescence decay curves. The application performance of the phosphor was improved by introducing Ga to substitute for In, and the blue shift of nearly 50 nm was explained by crystal field and nephelauxetic effects. At the same time, a 24% increase in the activation energy of thermal quenching of phosphors was obtained, which has been analyzed using the mechanism of phonon transition and the change of structural rigidity. Thus, the near-infrared emitting CaInGaGeO:0.07Cr phosphor was obtained, which has lower cost, higher emission intensity, and much better thermal stability, spreading the application of phosphors in plant far red light illumination, human body detection, and spectral conversion technology of silicon-based solar cells. Simultaneously, an example of a near-infrared plant illumination experiment is given, demonstrating that a cation substitution strategy based on crystal field control could be applied to tune spectral distribution and develop novel potential phosphors for practical optical application.