Electrospun strong, bioactive, and bioabsorbable silk fibroin/poly (L-lactic-acid) nanoyarns for constructing advanced nanotextile tissue scaffolds.

Bio-textiles have aroused attractive attentions in tissue engineering and regenerative medicine, and developing robust, bio-absorbable, and extracellular matrix (ECM) fibril-mimicking nanofibrous textiles is urgently required for the renewal of existing microfibrous textile-based scaffolds and grafts. In this study, an integrated electrospinning system consisting of one nanoyarn-forming unit and one hot stretching unit is reported to fabricate silk fibroin (SF)/poly (L-lactic-acid) (PLLA) nanofibrous yarns (nanoyarns). The hot stretching process is demonstrated to significantly improve the fiber alignment, crystallinity, and mechanical properties of SF/PLLA nanoyarns, compared to the unstretched controls. For instance, the fiber alignment degree of hot stretched 50/50 SF/PLLA nanoyarn has increased by 25%, and the failure strength has increased by 246.5%, compared with the corresponding un-stretched control. Increasing the SF/PLLA mass ratio is found to significantly decrease the crystallinity and mechanical properties, but notably increase the degradation rate and surface hydrophilicity of SF/PLLA nanoyarns. Different SF/PLLA nanoyarns are further meticulously interwoven with warp and weft directions to obtain several nanofibrous woven textiles. The results from cell characterization and subcutaneous implantation show that increasing the SF/PLLA mass ratio significantly improves the biological properties and effectively reduces the inflammatory response of nanoyarn-constructed textiles. Overall, this study demonstrates that our SF/PLLA nanoyarns with controllable physical, mechanical and biological performances are fantastic candidates for the designing and development of advanced nanoarchitectured textile tissue scaffolds.