Polyaspartic acid, 2-acrylamido-2-Methyl propane sulfonic acid and sodium alginate based biocompatible stimuli responsive polymer gel for controlled release of GHK-Cu peptide for wound healing.

Stimuli responsive polymer based on Polyaspartic acid, 2-Acrylamido-2-methylpropane sulfonic acid and sodium alginate (NaAlg) were synthesized using two cross-linkers Ethylene glycol dimethacrylate (EGDMA) and TMPTA (Trimethylolpropane triacrylate). The polymers were standardized and optimized to obtain a polymer with maximum swelling in distilled water, saline, glucose and solutions of varying pH. The synthesized polymer swelled well in distilled water, glucose solution and acidic- alkaline medium. The biocompatibility of the polymer was evaluated for blood compatibility and protein adsorption. The polymer with maximum swelling property was used for peptide release studies. The polymer was further used to study the peptide encapsulation and release efficiency of the polymeric material which was confirmed by FTIR, Scanning Emission Microscope and EDX. The encapsulation efficiency of the polymer for encapsulating (glycyl-l-histidyl-l-lysine-copper) GHK-Cu was observed to be 55.26% and peptide release of 51.84% was observed for Ethylene glycol dimethacrylate based polymer after 24 h whereas for Trimethylolpropane triacrylate based polymer the encapsulation efficiency was observed to be 49.6% and release was 39.01%. The EGDMA based polymer was further examined under studies in order to evaluate the efficiency of the synthesized polymer. The studies include wound closure, histopathological analysis, biochemical and toxicity assay. The material has shown promising results for both and studies.