Amine modified nano-silica was prepared via a one-pot route and under very mild conditions in water in oil microemulsion with a non-ionic surfactant to study the effect of changing the amount of N-[3-(Trimethoxysilyl)propyl]ethylenediamine (DA) added to the synthesis mixture on the characteristics of the obtained nanocomposite such as morphology, crystallinity, surface charge, particle size, surface area, and accordingly the effect of all of these factors on the efficiency of the nanocomposite for the removal of heavy metal ions, namely zinc, from aqueous solutions. XRD, SEM, TGA, BET, DLS, FTIR, and pH analysis were performed for samples and the results showed a strong effect for the amount of DA added to the synthesis mixture on the characteristics of the obtained nanocomposites. It was found that increasing the amount of DA added to the synthesis mixture increased the pH, hydrodynamic particle size obtained by dynamic light scattering analysis, and the particle size obtained by SEM. Sample prepared without the addition of DA (SNP) and the samples prepared with 1.5 mL of DA (SNP-1.5DA) showed a better adsorption performance compared to the samples prepared with 0.5 and 1.0 mL of DA (SNP-0.5DA and SNP-1.0DA, respectively). The main factor affecting the adsorption efficiency was found to be the available surface area for each nanocomposite, which was directly related to the degree of crystallinity as obtained by XRD analysis.

Download full-text PDF

Source
http://www.ncbi.nlm.nih.gov/pmc/articles/PMC8955496PMC
http://dx.doi.org/10.3390/nano12060947DOI Listing

Publication Analysis

Top Keywords

synthesis mixture
12
particle size
12
mixture characteristics
8
surface area
8
amount synthesis
8
samples prepared
8
one-pot synthesis
4
synthesis amine-functionalized
4
amine-functionalized nano-silica
4
nano-silica sol-gel
4

Similar Publications

Want AI Summaries of new PubMed Abstracts delivered to your In-box?

Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!