A biomimetic approach to evaluate mineralization of bioactive glass-loaded resin composites.

Purpose: This study explores novel solutions other than standard SBF for biomimetic evaluations of mineralization particularly for resin composites containing bioactive glass (BAG).

Methods: Experimental UDMA/TEGDMA resin composites with 0.0, 1.9, 3.8 or 7.7 vol% of 45S5 BAG fillers were prepared. Besides simulated body fluid (SBF) as control, the specimens were immersed in three other solutions either with bicarbonate which are Hank's balanced salt solution (HBSS) and cell culture medium (MEM), or without bicarbonate which is a novel Simple HEPES-containing Artificial Remineralization Promotion (SHARP) solution, for 3, 7 and 14 days. These solutions were then analyzed by ICP-OES and pH meter, and the surfaces of the BAG composites were analyzed by SEM, XRD and FTIR.

Results: ICP-OES revealed Ca and P concentration continuously decrease, while Si concentration increases with time in the solutions other than SBF, which showed almost unchanged elemental concentration. Only SHARP solution is able to maintain a constant pH over the immersion time. SEM, together with XRD and FTIR, showed nano-sized octacalcium phosphate (OCP) nanospheres formation on 3.8 and 7.7 vol% BAG composites after 14 days immersion in HBSS (500-600 nm) and MEM (300-400 nm). SHARP solution enabled OCP formation after 3 days and then self-assembled into urchin-like carbonated hydroxyapatite (CHA) microspheres encompassed with nanorods of 100 nm width and 8 µm length after 14 days of immersion for 7.7 vol% BAG composites.

Conclusion: This study suggests SHARP solution can evaluate mineralization biomimetically whereas CHA microspheres can be formed on BAG-containing resin composites.