Pressure-Induced Structural Behavior of Orthorhombic Mn(VO): Raman Spectroscopic and X-ray Diffraction Investigations.

The effect of high pressure on the structure of orthorhombic Mn(VO) is investigated using Raman spectroscopy and X-ray powder diffraction up to high pressures of 26.2 and 23.4 GPa, respectively. The study demonstrates a pressure-induced structural phase transition starting at 10 GPa, with the coexistence of phases in the range of 10-20 GPa. The sluggish first-order phase transition is complete by 20 GPa. Importantly, the new phase could be recovered at ambient conditions. Raman spectra of the recovered new phase indicate increased distortion and as a consequence the lowering of the local symmetry of the VO tetrahedra. This behavior is different from that reported for isostructural compounds Zn(VO) and Ni(VO) where both show stable structures, although almost similar anisotropic compression of the unit cell is observed. The transition observed in orthorhombic Mn(VO) could be due to the internal charge transfer between the cations, which favors the structural transition at lower pressures and the eventual recovery of the new phase even upon pressure release in comparison to other isostructural compounds. The experimental equation of state parameters obtained for orthorhombic Mn(VO) match excellently with empirically calculated values reported earlier.