Electrodeposition of Complex High Entropy Oxides via Water Droplet Formation and Conversion to Crystalline Alloy Nanoparticles.

A combination of electrodeposition and thermal reduction methods have been utilized for the synthesis of ligand-free FeNiCo alloy nanoparticles through a high-entropy oxide intermediate. These phases are of great interest to the electrocatalysis community, especially when formed by a sustainable chemistry method. This is successfully achieved by first forming a complex five element amorphous FeNiCoCrMn high-entropy oxide (HEO) phase via electrodeposition from a nanodroplet emulsion solution of the metal salt reactants. The amorphous oxide phase is then thermally treated and reduced at 570-600 °C to form the crystalline FeNiCo alloy with a separate CrMnO cophase. The FeNiCo alloy is fully characterized by scanning transmission electron microscopy and energy-dispersive X-ray spectroscopy elemental analysis and is identified as a face-centered cubic crystal with the lattice constant = 3.52 Å. The unoptimized, ligand-free FeNiCo NPs activity toward the oxygen evolution reaction is evaluated in alkaline solution and found to have an ∼185 mV more cathodic onset potential than the Pt metal. Beyond being able to synthesize highly crystalline, ligand-free FeNiCo nanoparticles, the demonstrated and relatively simple two-step process is ideal for the synthesis of tailor-made nanoparticles where the desired composition is not easily achieved with classical solution-based chemistries.