The study on the effect of flotation purification on the performance of α-hemihydrate gypsum prepared from phosphogypsum.

Phosphogypsum (PG) is a massive industrial solid waste. In this paper, PG was purified by flotation method, and α-hemihydrate gypsum (α-HH) was prepared by the autoclaving method. The morphology of α-HH was adjusted by adding different doses of Maleic acid and Aluminium sulfate. The results showed that after flotation purification, the impurity content in PG was significantly reduced, the soluble phosphorus content decreased from 0.48 to 0.07%, the PG purity increased from 73.12 to 94.37%, and the PG whiteness risen from 19.4 to 40.5. Then the performance of α-HH prepared from PG before and after purification was compared. Fixing the amount of aluminium sulfate at 0.2 wt%, the reaction temperature at 140 °C, and the reaction time at 120 min, the average length/diameter ratio of α-HH crystals decreased from 7.2 to 0.6 as the amount of Maleic acid increased from 0 to 0.17 wt%. When the amount of Maleic acid was 0.13 wt%, the α-hemihydrate gypsum reached the best mechanical properties. The mechanical strength of high strength gypsum prepared from PG concentrate was significantly better than that of raw PG, indicating that flotation purification can effectively improve the performance of PG. In this study, a new method of PG purification and resource utilization was proposed.