Microstructure and Mechanical Properties of Welded Joints of 1.4462 Duplex Steel Made by the K-TIG Method.

K-TIG (Keyhole Tungsten Inert Gas) method is a new, emerging welding technology that offers a significant acceleration of the joining process, even for very thick plates. However, its potential for welding of certain materials is still unknown. Particularly challenging are duplex steels as this technology does not allow the use of a filler material, which is crucial for these steels and for weld joint microstructure adjustment. In order to demonstrate the suitability of this technology for single-pass welding of 1.4462 duplex steel detailed studies of the microstructure of the weld joints obtained for different linear energies were carried out and discussed with respect to their mechanical properties. According to the results obtained, the heat-affected zone (HAZ) shows a microstructure similar to the HAZ of duplex steel welded with the traditional TIG multi-pass methods. However, the weld, due to the lack of filler material, had a microstructure different to that typical for duplex steel welded joints and was also characterized by an increased content of ferrite. However, all joints, both in terms of microstructure and mechanical properties, met the requirements of the relevant standards. Moreover, the K-TIG process can be carried out in the linear energy range typical of duplex steel welding, although further optimization is needed.