Microstructure and Oxidation Behavior of Fe-25Mn-9Al-8Ni-1C-xTi Alloy Prepared by Vacuum Arc Melting.

Materials (Basel)

School of Materials and Chemical Engineering, Xi'an Technological University, Xi'an 710021, China.

Published: December 2021

In this study, Fe-25Mn-9Al-8Ni-1C-xTi alloy (x = 0, 0.1, 0.2, 0.3, 0.4 wt.%) was prepared by vacuum arc melting, and the corresponding microstructure and oxidation behavior at 600 °C were studied. The results show that Fe-25Mn-9Al-8Ni-1C-xTi alloy mainly contains austenite phase, ferrite phase and TiC phase. With Ti content increasing, the austenite phase content decreases, while the contents of ferrite phase and TiC phase increase. The oxidation performance test results show that the addition of Ti element greatly reduces the oxidation weight gain of the alloys at the initial oxidation stage. With the extension of the oxidation time and the further increase of the Ti content, the alloys oxidation weight gain shows a trend of first increasing and then decreasing. When the Ti content is 0.2 wt.%, the oxidation weight gain of this series of alloy reaches the lowest value during the stable oxidation period. Compared with Fe-25Mn-9Al-8Ni-1C alloy, its weight gain per unit area is reduced by 21.1%. Fe-25Mn-9Al-8Ni-1C-xTi alloy oxide layer exhibits a double-layer structure. The outer oxygen layer is mainly loose iron-oxides, while in the inner oxygen layer, the oxides are mainly composed of manganese-oxides and aluminum-oxides, which are relatively dense.

Download full-text PDF

Source
http://www.ncbi.nlm.nih.gov/pmc/articles/PMC8703821PMC
http://dx.doi.org/10.3390/ma14247722DOI Listing

Publication Analysis

Top Keywords

fe-25mn-9al-8ni-1c-xti alloy
16
weight gain
16
oxidation weight
12
microstructure oxidation
8
oxidation behavior
8
prepared vacuum
8
vacuum arc
8
arc melting
8
oxidation
8
austenite phase
8

Similar Publications

Want AI Summaries of new PubMed Abstracts delivered to your In-box?

Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!