Modified zaccagnaite layered double hydroxide (LDH) type films were synthesized on steel substrates by pulsed electrochemical deposition from aqueous solutions. The resulting films were characterized by X-ray diffraction, scanning electron microscopy/X-ray dispersive spectroscopy, and Fourier transform infrared spectroscopy. Structural characterization indicated a pure layered double hydroxide phase; however, elemental analysis revealed that the surface of the films contained Zn:Al ratios outside the typical ranges of layered double hydroxides. Layer thickness for the deposited films ranged from approximately 0.4 to 3.0 μm. The corrosion resistance of the film was determined using potentiodynamic polarization experiments in 3.5 wt.% NaCl solution. The corrosion current density for the coatings was reduced by 82% and the corrosion potential was shifted 126 mV more positive when 5 layers of modified LDH coatings were deposited onto the steel substrates. A mechanism was proposed for the corroding reactions at the coating.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC8658376 | PMC |
| http://dx.doi.org/10.3390/ma14237389 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Mechanistic Insights into the Corrosion Inhibition Performance of Eco-Friendly Nitrogen and Boron Co-Doped Carbon Dots for Mild Steel in a 15% HCl Solution.
Langmuir
January 2025
Department of Physics and Astronomy College of Science, King Saud University, P. O.Box 2455, Riyadh 11451, Saudi Arabia.
A novel and eco-friendly route to synthesize boron, nitrogen codoped carbon dots using aniline, citric acid, and boric acid as precursor materials has been used successfully to reduce mild steel corrosion. This report describes the detailed weight-loss experiments, electrochemical measurements, and surface morphology analysis conducted to explore the efficacy of B,N-CDs as a highly effective corrosion controller for mild steel (MS) protection in 15% hydrochloric acid (HCl). The findings specify that B,N-CDs significantly decreased the corrosion of MS and attained an inhibition capacity of up to 96.
View Article and Find Full Text PDF(ZnO) Cluster Decorated 2D Porous CN Materials as Efficient Solar Cells.
J Phys Chem A
January 2025
College of Physics Science and Technology, Yangzhou University, Yangzhou 225009, China.
Developing high-performance solar cells is a practical way to improve clean energy conversion efficiency. However, the performance of solar cells faces challenges such as fast carrier combination, poor stability, and limited solar light harvesting. Herein, we propose a strategy by decorating periodic holes in two-dimensional (2D) porous carbon-nitrogen (CN) materials with a zero-dimensional (0D) semiconducting (ZnO) cluster.
View Article and Find Full Text PDFAnticorrosion properties of ionic liquid functionalized graphene oxide epoxy composite coating on the carbon steel for CCUS environment.
Environ Sci Pollut Res Int
January 2025
Department of Chemical Engineering, Indian Institute of Technology Guwahati, Guwahati, 781039, Assam, India.
The adoption of carbon capture, utilization, and storage (CCUS) technology is increasingly prevalent, driven by the global initiative to conserve energy and reduce emissions. Nevertheless, CCUS has the potential to induce corrosion in equipment, particularly in high-pressure environments containing carbon dioxide (CO). Therefore, anti-corrosion protection is necessary for the metal utilized for CO production and storage equipment.
View Article and Find Full Text PDFInfluence of sterilization and exposure to the Ringer's solution on physicochemical properties of nitrocarburized 316 LVM steel.
Acta Bioeng Biomech
September 2024
Faculty of Materials Science and Engineering, Warsaw University of Technology, Warsaw, Poland.
The aim of the study was to investigate the influence of the nitrocarburizing process carried out in low temperature plasma using the active screen at 440 °C on the structure and physicochemical properties of the 316LVM steel. In the paper, results of micro-structure and phase composition of the layers, roughness, and surface wettability, potentiodynamic pitting corrosion resistance, penetration of ions into the solution as well as biological tests were present. The studies were conducted for the samples of both mechanically polished and nitrocarburized surfaces, after sterilization, and exposure to the Ringer's solution.
View Article and Find Full Text PDFEnhancing the Mechanical and Adhesive Properties of Polyurethane Adhesives with Propylene Oxide-Modified Ethylenediamine (PPO-EDA).
Polymers (Basel)
January 2025
Green Chemistry & Materials Group, Korea Institute of Industrial Technology (KITECH), Cheonan 31056, Republic of Korea.
This study explores the use of propylene oxide-modified ethylenediamine (PPO-EDA) as a novel crosslinker and chain extender in polyurethane (PU) adhesives. PPO-EDA was synthesized and compared with ,-dimethylethylenediamine (DMEDA) to assess its impact on mechanical properties and adhesion performance. Key parameters such as NCO conversion, tensile strength, and lap shear strength were thoroughly evaluated.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!