Purpose: To investigate the bond strength and durability of a novel dual-curing composite cement to zirconia under different curing conditions.
Materials And Methods: Zirconia plates of different thickness (0.5, 1, and 2 mm) were bonded with either a novel dual-curing composite cement (Panavia V5, PV5, Kuraray Noritake) or a traditional one (RelyX Ultimate, RUL, 3M Oral Care; Multilink Automix, MLA, Ivoclar Vivadent), in light-, self-, or dual-curing mode. Bonded specimens were subjected to shear bond strength (SBS) tests after 24 h of water storage or after artificially aging by 20,000 thermal cycles plus 150 days of water storage. The degree of conversion (DC) of the composite cements under different curing conditions was measured by Fourier transform infrared (FTIR) spectroscopy. The irradiance and translucency of the zirconia plates of different thickness were also investigated.
Results: The irradiance and translucency of zirconia decreased significantly with increasing thickness (p = 0.00). Both before and after aging, SBS of PV5 in self-curing mode was significantly higher than that of RUL (p = 0.07 before aging and 0.02 after aging) and MLA (p = 0.00 both before and after aging). However, for the three composite cements, light- and dual curing yielding the same SBSs for a constant Y-TZP thickness (p > 0.05). The FTIR analysis showed that, for all three dual-curing composite cements examined in this study, the mean DC values obtained in dual-curing mode were lower than those achieved in light-curing mode (p = 0.00 for PV5, RUL, and MLA). For RUL and MLA, lower mean DC values were obtained in self-curing than dual-curing mode (p = 0.00 for both RUL and MLA), while the DC values of PV5 showed no significant difference between self-curing and dual-curing mode (p = 0.33).
Conclusion: When the photoactivation time is 60 s and the thickness of the zirconia restoration is less than 2 mm, it is safe to use the two traditional dual-curing composite cements RUL and MLA and PV5 for bonding zirconia. However, when the light exposure time is insufficient, PV5 provides improved bond strength and durability to zirconia.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.3290/j.jad.b2288181 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
The Impact of Different Irrigation Protocols on the Bond Strength of Self-Adhesive Resin Cement to Radicular Dentin.
Acta Stomatol Croat
September 2024
Department of Endodontics and Restorative Dentistry, University of Zagreb School of Dental Medicine, Zagreb, Croatia.
Objective: The objective of the study was to investigate the influence of different irrigation protocols on the shear bond strength (SBS) of self-adhesive resin cement (SARC) on primed radicular dentin.
Methods: Radicular dentin slabs (N=58) were embedded in acrylic. Subsequently, they were polished and randomly assigned to five experimental groups (N=8-12) and one control group, CG (N=8).
The purpose of this study was to evaluate the influence of simplified ceramic surface treatments on the microshear bond strength (μSBS) of 2 resin cements to a zirconia-reinforced lithium silicate (ZLS) material. Blocks of ZLS were sectioned to obtain a total of 90 specimens (1.5 mm thick), which were assigned to 9 different surface treatment protocols (n = 10).
View Article and Find Full Text PDFEffect of resin cement viscosities and surface roughness on shear bond strength of conditioned polymer infiltrated ceramic network.
Photodiagnosis Photodyn Ther
October 2024
Department of Prosthetic Dental Sciences, College of Dentistry Prince Sattam Bin Abdulaziz University, 11942 Alkharj, Saudi Arabia. Electronic address:
Background: Hybrid ceramics bonding with the dentinal substrate is crucial for clinical success and longevity. To enhance adhesion, the surface of ceramic restorations is modified through various conditioning techniques AIM: Effect of Different Surface Conditioners Erbium-doped yttrium aluminum garnet (ER: YAG) laser and Low-level laser therapy (LLLT) activated Methylene blue (MB) on the surface roughness (Ra) and shear bond strength (SBS) of Polymer infiltrating ceramic network (PICN) discs bonded using different viscosity resin cement before and after thermal aging.
Material And Methods: One hundred and fifty human central incisors and one hundred and fifty-three PICN discs were prepared.
Effects of Etching Time and Ethanol Wet Bonding on Bond Strength and Metalloproteinase Activity in Radicular Dentin.
J Clin Med
April 2024
Department of Surgical Sciences, Dental School Lingotto, University of Turin, 10100 Turin, Italy.
(1) : The objective of this in vitro study was to evaluate the impact of different etching times and ethanol pre-treatments on the immediate bond strength of a hydrophilic multi-mode universal adhesive (Clearfil Universal Bond Quick, Kuraray, UBQ) and on the consequent gelatinolytic activity of metalloproteinases (MMPs) on radicular dentin. (2) : Sixty single-root teeth were selected and divided into four groups according to the adhesive protocol applied for fiber post cementation: (G1) 15 s HPO application + UBQ; (G2) 30 s HPO application + UBQ; (G3) 15 s HPO application + ethanol pre-treatment + UBQ; (G4) 30 s HPO + ethanol pre-treatment + UBQ. After adhesive procedures, fiber posts were luted into the post space with a dual-curing cement (DC Core, Kuraray) and light-cured for 40 s.
View Article and Find Full Text PDFResidual stresses in glass crowns generated by polymerization and water sorption of resin cements.
Dent Mater J
June 2024
Department of Operative Dentistry, Tsurumi University School of Dental Medicine.
This study investigated residual stresses in glass crowns cemented with resin cements. Glass caps were cemented to cylindrical cores using a conventional resin composite cement, a self-adhesive resin cement, or a methyl methacrylate (MMA)-based cement in dual-cure or self-cure mode. The cemented caps were stored in 37°C water for 28 days, and stresses on the cap surface were repeatedly measured.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!