The aim of the study was to analyse the colour fastness of 3D printed samples that could be used as decorative or household items. Such items are often fabricated with 3D printing. The colour of filaments affects not only the mechanical properties, but also the appearance and user satisfaction. Samples of biocomposite filaments (PLA and PLA with added wood and hemp fibres) were used. First, the morphological properties of the filaments and 3D printed samples were analysed and then, the colour fastness against different agents was tested (water, oil, detergent, light and elevated temperature). Finally, the dynamic mechanical properties of the filaments and 3D printed samples were determined. The differences in the morphology of the filaments and 3D printed samples were identified with SEM analysis. The most obvious differences were observed in the samples with wood fibres. All printed samples showed good resistance to water and detergents, but poorer resistance to oil. The sample printed with filaments with added wood fibres showed the lowest colour fastness against light and elevated temperatures. Compared to the filaments, the glass transition of the printed samples increased, while their stiffness decreased significantly. The lowest elasticity was observed in the samples with wood fibres. The filaments to which hemp fibres were added showed the reinforcement effect. Without the influence on their elasticity, the printed samples can be safely used between 60 and 65 °C.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC8588260 | PMC |
| http://dx.doi.org/10.3390/polym13213738 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Sub-millimeter fiberscopic robot with integrated maneuvering, imaging, and biomedical operation abilities.
Nat Commun
December 2024
Department of Electronic and Computer Engineering, Hong Kong University of Science and Technology, Hong Kong SAR, China.
Small-scale continuum robots hold promise for interventional diagnosis and treatment, yet existing models struggle to achieve small size, precise steering, and visualized functional treatment simultaneously, termed an "impossible trinity". This study introduces an optical fiber-based continuum robot integrated imaging, high-precision motion, and multifunctional operation abilities at submillimeter-scale. With a slim profile of 0.
View Article and Find Full Text PDFIn vitro evaluation of frozen thawed kangayam bull semen enriched with antioxidants.
Pol J Vet Sci
September 2024
Department of Clinics, Veterinary College and Research Institute, Tamil Nadu Veterinary and Animal Sciences University, Namakkal-637 001, India.
The aim of this study was to assess the in vitro penetration rate of antioxidant enriched frozen thawed Kangayam bull semen. For the current investigation, 5-7-year-old Kangayam bulls were used. The semen was collected twice per week and two ejaculates were collected each time.
View Article and Find Full Text PDFThe Effect of Thermal Cycle on Hot Cracking Evolution and Formation Mechanism in Thin Wall, Single Layer, and Cubic Samples of High-Strength Al-Cu-Mg-Mn Alloys Fabricated by Laser Powder Bed Fusion.
3D Print Addit Manuf
December 2024
School of Optical and Electronic Information, Huazhong University of Science and Technology, Wuhan, P.R. China.
Thermal cracking is one of the serious issues that deteriorates the processibility of laser powder bed fusion (LPBF) high-strength aluminum components. To date, the effects of processing parameters on crack formation are still not well understood. The purpose of this study is to understand the correlation between the thermal cycle and the hot cracking during LPBF of Al-Cu-Mg-Mn alloys.
View Article and Find Full Text PDFSurface Structure Modification in Fused Filament Fabrication (FFF) Multi-Material Printing for Medical Applications: Printing of a Hand Prosthesis.
3D Print Addit Manuf
December 2024
Institute of Materials Science and Engineering, Faculty of Mechanical Engineering, Lodz University of Technology, Łódź, Poland.
Fused Filament Fabrication (FFF) printing is one of the most all-purpose manufacturing techniques, allowing many complicated parts to be obtained at lower cost. This is especially important in prosthetics, where more complex prostheses, especially of a hand, can cause enormous expense. However, providing the full functionality of a prosthesis often requires combining materials with different properties, such as rigidity and flexibility.
View Article and Find Full Text PDFMaximizing Mechanical Performance of 3D Printed Parts Through Process Parameter Optimization.
3D Print Addit Manuf
December 2024
Department of Thermodynamics, Mechanical Engineering and Energy, University of Zagreb, Faculty of Chemical Engineering and Technology, Zagreb, Croatia.
The article discusses the importance of optimizing process parameters in 3D printing to achieve better mechanical properties of printed parts. It emphasizes the material extrusion 3D printing technology and some of the most commonly used materials, acrylonitrile butadiene styrene (ABS) and polyethylene terephthalate glycol (PETG). Optimizable process parameters such as, print angle, outer layer number, extruder flow ratio, extrusion (nozzle) temperature, and layer thickness are examined.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!