This research aimed to evaluate the effect of adding different polymeric waste percentages and types on the physical, mechanical, thermal, and durability properties of soil-cement bricks. Tire and polyethylene terephthalate (PET) waste were evaluated at 1.5 and 3.0% (mass/mass). The soil was characterized in terms of shrinkage, compaction, consistency limits, particle size, and chemical analyses, whereas the waste particles were submitted to morphological characterization. The bricks were produced in an automatic press with a 90:10 (mass/mass) soil:cement ratio. The soil-cement bricks were characterized by density, moisture, water absorption, loss of mass by immersion, compressive strength, thermal conductivity, and microstructural analysis. PET waste stood out for its use as reinforcement in soil-cement bricks. The best performance was obtained for bricks reinforced with 1.5% PET, which showed a significant compressive strength improvement, meeting the marketing standards criteria, even after the durability test, as well as obtaining the lowest thermal conductivity values. The percentage increase from 1.5 to 3.0% fostered a significant water absorption and loss of mass increase, as well as a significant compressive strength reduction of the bricks.
In the search for better constructive efficiency and a reduction of the waste of construction materials, several researches have been performed in the last years around the world. Red ceramic blocks are artifacts widely used in civil construction around the world, and they result in a great consumption of raw materials and energy. The great innovation of this research was the development of ceramic blocks through an innovative method of pressing and dosing materials, replacing the traditional stage of extrusion in the manufacture of ceramics.
The need for environmental preservation requires civil engineering to reach new concepts and technical solutions aiming at the sustainability of its activities and products. In this context, this study aimed to evaluate the effect of using different types and percentages of vegetable particles on the physical, mechanical, and thermal properties of soil-cement bricks. Bamboo, rice husk, and coffee husk particles at 1.
This research aimed to evaluate the effect of adding different polymeric waste percentages and types on the physical, mechanical, thermal, and durability properties of soil-cement bricks. Tire and polyethylene terephthalate (PET) waste were evaluated at 1.5 and 3.
The ever-growing consumption and improper disposal of non-biodegradable plastic wastes is bringing worrisome perspectives on the lack of suitable environmentally correct solutions. Consequently, an increasing interest in the circular economy and sustainable techniques is being raised regarding the management of these wastes. The present work proposes an eco-friendly solution for the huge amount of discarded polyethylene terephthalate (PET) wastes by addition into soil-cement bricks.
Northern Fluminense State University, Laboratory of Advanced Materials, Group of Ceramic Materials, 28013-602 Campos dos Goytacazes, RJ, Brazil. Electronic address:
This investigation focuses on the reuse of grits waste as a raw material for replacing Portland cement by up to 30 wt.% in soil-cement bricks. The grits waste was obtained from a cellulose factory located in south-eastern Brazil.