Effect of Thermal Properties of Aggregates on the Mechanical Properties of High Strength Concrete under Loading and High Temperature Conditions.

The effect of the thermal properties of aggregates on the mechanical properties of high-strength concrete was evaluated under loading and high-temperature conditions. For the concrete, granite was selected as a natural aggregate, and ash-clay and clay as lightweight aggregates. The mechanical properties of the concrete (stress-strain, compressive strength, elastic modulus, thermal strain, and transient creep) were evaluated experimentally under uniform heating from 20 to 700 °C while maintaining the load at 0, 20, and 40% of the compressive strength at room temperature. Experimental results showed that the concrete containing lightweight aggregates had better mechanical properties, such as compressive strength and elastic modulus, than that of the concrete with a granite aggregate at high temperature. In particular, the concrete containing lightweight aggregates exhibited high compressive strength (60-80% of that at room temperature) even at 700 °C. Moreover, the concrete containing granite exhibited a higher thermal strain than that containing lightweight aggregates. The influence of the binding force under loaded conditions, however, was found to be larger for the latter type. The transient creep caused by the loading was constant regardless of the aggregate type below 500 °C but increased more rapidly when the coefficient of the thermal expansion of the aggregate was above 500 °C.