CO/N Gas Separation Using Pebax/ZIF-7-PSf Composite Membranes.

In this study, we mixed the zeolitic imidazolate framework-7 (ZIF-7) with poly(ether-b-amide) 2533 (Pebax-2533) and used it as a selective layer for a composite membrane. We prepared the composite membrane's substrate using polysulfone (PSf), adjusted its pore size using polyethylene glycol (PEG), and applied polydimethylsiloxane (PDMS) to the gutter layer and the coating layer. Then, we investigated the membrane's properties of gases by penetrating a single gas (N, CO) into the membrane. We identified the peaks and geometry of ZIF-7 to determine if it had been successfully synthesized. We confirmed that ZIF-7 had a BET surface area of 303 m/g, a significantly high Langmuir surface area of 511 m/g, and a high CO/N adsorption selectivity of approximately 50. Considering the gas permeation, with ZIF-7 mixed into Pebax-2533, N permeation decreased from 2.68 GPU in a pure membrane to 0.43 GPU in the membrane with ZIF-7 25 wt%. CO permeation increased from 18.43 GPU in the pure membrane to 26.22 GPU in the ZIF-7 35 wt%. The CO/N ideal selectivity increased from 6.88 in the pure membrane to 50.43 in the ZIF-7 25 wt%. Among the membranes, Pebax-2533/ZIF-7 25 wt% showed the highest permeation properties and the characteristics of CO-friendly ZIF-7.