Electrospun ethyl cellulose/poly caprolactone/gelatin nanofibers: The investigation of mechanical, antioxidant, and antifungal properties for food packaging.

The purpose of the present research was to fabricate ethylcellulose (ECL)/polycaprolactone (PCL)/gelatin (GEL) electrospun nanofibers containing Zataria multiflora essential oil (ZEO) and zinc oxide nanoparticle (ZnO) to provide an appropriate substrate for food packaging. The ECL/PCL/GEL was incorporated with ZEO and ZnO at the concentrations of 10, 20, 30 and 50 wt% and 3 wt%, respectively. The results of ECL/PCL/GEL/ZEO/ZnO nanofiber exhibited uniform morphology with a mean diameter ranging from 361.85 ± 18.7 to 467.33 ± 14.50 nm and enhanced thermal stability. The ECL/PCL/GEL/ZEO/ZnO nanofiber had the highest mechanical parameters, such as young's modulus (437.49 ± 18), tensile strength (7.88 ± 0.7), and elongation at break (5.02 ± 0.6) and water contact angle (61.13 ± 0.5), compared with the other nanofibers. The cell viability during 48 and 72 h was obtained to be about more than 80% for all the nanofibers. Additionally, the ECL/PCL/GEL incorporated with 50% ZEO and 3% ZnO displayed the highest antioxidant activity (34.61 ± 1.98%) and antifungal properties against Penicillium notatum and Aspergillus niger. In general, the ECL/PCL/GEL with the weight ratio of 20:70:10 nanofiber incorporated with 30% ZEO and 3% ZnO was obtained to have appropriate mechanical, antioxidant, and antimicrobial properties and thermal stability.