Determination of Fire Parameters of Polyamide 12 Powder for Additive Technologies.

The use of additive technologies keeps growing. Increasingly, flammable powder materials are also used in additive technologies, and there is a risk of explosion or fire when using them. The current article deals with the determination of fire parameters of a powder sample of polyamide Sinterit PA12 Smoth in accordance with the EN 14034 and EN ISO/IEC 80079-20-2 standards. For that purpose, a sample at a median size of 27.5 µm and a humidity of 0% wt. was used. The measurements showed that the maximum explosion pressure of the PA12 polyamide sample was 6.78 bar and the value of the explosion constant K was 112.2 bar·m·s. It was not possible to determine the MIT value of the settled dust, since the melting point of polyamide sample is low. The MIT of the dispersed dust was 450 °C. Based on the measured results, it can be stated that the powdered polyamide PA12 poses a risk in terms of explosions and fires. Therefore, when using polyamide PA12 in additive technologies, it is necessary to ensure an effective explosion prevention.