External Marginal Gap Variation and Residual Fracture Resistance of Composite and Lithium-Silicate CAD/CAM Overlays after Cyclic Fatigue over Endodontically-Treated Molars.

The purpose of this in vitro study was to evaluate the external marginal gap variation with a 3D quantitative method and the residual fracture resistance after cyclic fatigue in endodontically treated molars restored with overlays of different materials, with and without fiber posts-supported buildups. Forty-eight human maxillary molars were selected, endodontically treated, prepared with standardized MOD cavities and randomly allocated into 6 study groups considering the "core strategy" (build-up with composite resin; build-up with composite resin supported by a fiber post); and the "restorative material" of the indirect adhesive overlay (GrandioBlocks, Voco; Cerasmart, GC; CeltraDuo, Dentsply). All procedures were executed according with manufacturers guidelines. Micro-CT analysis prior and after cyclic fatigue were executed, followed by scanning electron microscope analysis and fracture resistance test. The Two-Way ANOVA analysis showed that interfacial gap progression was significantly influenced by the "core strategy" ( 0.01) but not of "restorative material" ( 0.59). Concerning fracture resistance, "restorative material" was statistically significant ( 0.01), while "core strategy" ( 0.63) and the interaction ( = 0.84) were not. In conclusion, the fiber post presence within the build-up promoted a lower interfacial gap opening after fatigue, evaluated through micro-CT scans. In terms of fracture resistance, teeth restored with Cerasmart and Celtra Duo were statistically similar, but superior to GrandioBlocks.