In this study, we demonstrated a facile method to prepare a novel SnOmicroporous rod with various microstructures by controlling NaOH molarities in precursor synthesis processes. Four different molarities of NaOH solution (0.005 M, 0.048 M, 0.12 M and 0.5 M) were used together with o-phthalic acid in Sn-MOF synthesis to determine the effect of ligand [o-CHCO222-] concentration on microstructure evolution. It was found that increasing NaOH molarity can effectively decrease the size of Sn-MOF rods. Then, the SnOmicroporous rods were obtained by calcinating the as-prepared Sn-MOF as microstructures. Under an optimized experimental condition (NaOH molarity of 0.12 M), the SnOrods shows a modest initial coulombic efficiency of 61.3% with a high reversible sodium storage capacity of 503 mAh gafter 150 cycles at 50 mA g. Moreover, an impressive reversible sodium storage capacity of 206 mAh gcan be obtained at long-term cycling performance (800 cycles at current density of 2 A g). Effects of morphologies to electrochemical performances have been further discussed in aspects of intrinsic resistance, pseudocapacitive contribution, surface area and porous structure and microstructural stability, and the enhanced electrochemical performance could be attributed to factors of enhanced pseudocapacitive charge contribution, optimized microstructures, and structural stability, which ensure the SnO-0.12 M to have a good rate performance and cyclability. This nanoscale-engineering method adopted here could be a promising path to fabricate SnO-based anodes with novel microstructures for sodium storage applications.

Download full-text PDF

Source
http://dx.doi.org/10.1088/1361-6528/ac1c21DOI Listing

Publication Analysis

Top Keywords

sodium storage
16
naoh molarities
8
snomicroporous rod
8
naoh molarity
8
reversible sodium
8
storage capacity
8
naoh
5
molarities microstructure
4
sodium
4
microstructure sodium
4

Similar Publications

Want AI Summaries of new PubMed Abstracts delivered to your In-box?

Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!