Assessment of Bond Integrity, Durability, and Degree of Conversion of a Calcium Fluoride Reinforced Dentin Adhesive.

Our study aimed to synthesize and compare the mechanical properties and dentin interaction of two adhesives; experimental adhesive (EA) and EA containing 5 wt.% calcium fluoride (CaF) nano-crystals (CaF adhesive-CAFA). CaF nano-crystals were synthesized by reacting two solutions (containing calcium and fluoride) in a glass chamber using a heated air system. The EA was produced using a mix of monomers, photo-initiators, camphorquinone, and electron initiators. The synthesized CaF nano-crystals were centrifuged to guarantee that inside the adhesive there is homogenized dispersion of the filler particles. Their integration in the EA yielded two groups; Gp-1: EA (without CaF, control) and Gp-2: (5 wt.% CaF containing adhesive, CAFA). Sixty teeth were prepared and set to form bonded specimens using the two adhesives. The CaF nano-crystals were irregularly shaped with an average particle size of 30-200 nm. The highest μTBS values were obtained for CAFA-non-thermocycled (NTC) samples (32.63 ± 3.15), followed by EA-NTC (31.80 ± 3.75) specimens. On thermocycling (TC), both adhesive groups presented lower μTBS values (CAFA-TC: 29.47 ± 3.33 and EA-TC: 24.04 ± 3.69). Hybrid layer (HL) formation and resin tags of varying depths were perceived for both adhesive groups. The EDX analysis demonstrated the presence of carbon (C), silica (Si), calcium (Ca), and fluoride (F) for CAFA group. Micro-Raman spectroscopy revealed distinct peaks for CaF nano-crystals. The CAFA group presented the greatest DC. The addition of CaF nano-crystals in the adhesive caused improved bond μTBS and DC. The incorporation also demonstrated suitable dentin interaction, depicted by appropriate HL and resin tag development.