In this paper, Al-Fe-Si-Zn-Cu (AA8079) matrix composites with several weight percentages of BC (0, 5, 10, and 15) were synthesized by powder metallurgy (PM). The essential amount of powders was milled to yield different compositions such as AA8079, AA8079-5 wt.%BC, AA8079-10 wt.%BC, and AA8079-15 wt.%BC. The influence of powder metallurgy parameters on properties' density, hardness, and compressive strength was examined. The green compacts were produced at three various pressures: 300 MPa, 400 MPa, and 500 MPa. The fabricated green compacts were sintered at 375 °C, 475 °C, and 575 °C for the time period of 1, 2 and 3 h, respectively. Furthermore, the sintered samples were subjected to X-ray diffraction (XRD) analysis, Energy Dispersive Analysis (EDAX), and Scanning Electron Microscope (SEM) examinations. The SEM examination confirmed the uniform dispersal of BC reinforcement with AA8079 matrix. Corrosion behavior of the composites samples was explored. From the studies, it is witnessed that the rise in PM process parameters enhances the density, hardness, compressive strength, and corrosion resistance.

Download full-text PDF

Source
http://www.ncbi.nlm.nih.gov/pmc/articles/PMC8347984PMC
http://dx.doi.org/10.3390/ma14154315DOI Listing

Publication Analysis

Top Keywords

powder metallurgy
12
corrosion behavior
8
matrix composites
8
aa8079 matrix
8
density hardness
8
hardness compressive
8
compressive strength
8
green compacts
8
microstructure mechanical
4
mechanical properties
4

Similar Publications

Want AI Summaries of new PubMed Abstracts delivered to your In-box?

Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!