Effect of lithium disilicate ceramic thickness, shade and translucency on transmitted irradiance and knoop microhardness of a light cured luting resin cement.

This in vitro study evaluates the influence of pressed lithium disilicate thickness, shade and translucency on the transmitted irradiance and the Knoop microhardness (KHN) of a light-cured resin cement at two depths. One hundred and thirty-five ceramic discs of IPS e.max Press (Ivoclar Vivadent) were fabricated and divided into twenty-seven groups (n = 5) according to the association between translucency: HT (hight translucency), LT (low translucency), and MO (medium opacity); shade: BL2, A1 and A3.5; and thickness: 0.5 mm, 1.5 mm, and 2.0 mm. One side of each ceramic disc was finished, polished and glazed. The irradiance (mW/cm²) of a multiwave LED light curing unit (Valo, Ultradent) was evaluated with a potentiometer (Ophir 10ª-V2-SH, Ophir Optronics) without (control group) or with interposition of ceramic samples. The microhardness of Variolink Esthetic LC resin cement (Ivoclar Vivadent) was evaluated after 24 h at two depths (100 μm and 700 μm). Data were submitted to ANOVA followed by Tukey's test (α = 0.05). Irradiance and KHN were significantly influenced by ceramic thickness (p < 0.0001), shade (p < 0.001), translucency (p < 0.0001) and depth (p < 0.0001). Conclusions: the interposition of increasing ceramic thicknesses significantly reduced the irradiance and microhardness of resin cement. Increased depth in the resin cement showed significantly reduced microhardness for all studied groups. Increased ceramic opacity reduced the KHN of the resin cement at both depths for all ceramic thicknesses and shades.