Crystal Growth and Characterization of n-GaN in a Multiple Quantum Shell Nanowire-Based Light Emitter with a Tunnel Junction.

Here, we systematically investigated the growth conditions of an n-GaN cap layer for nanowire-based light emitters with a tunnel junction. Selective-area growth of multiple quantum shell (MQS)/nanowire core-shell structures on a patterned n-GaN/sapphire substrate was performed by metal-organic vapor phase epitaxy, followed by the growth of a p-GaN, an n/ p-GaN tunnel junction, and an n-GaN cap layer. Specifically, two-step growth of the n-GaN cap layer was carried out under various growth conditions to determine the optimal conditions for a flat n-GaN cap layer. Scanning transmission electron microscopy characterization revealed that n-GaN can be uniformly grown on the -plane sidewall of MQS nanowires. A clear tunnel junction, involving 10-nm-thick p-GaN and 3-nm-thick n-GaN, was confirmed on the nonpolar -planes of the nanowires. The Mg doping concentration and distribution profile of the p-GaN shell were inspected using three-dimensional atom probe tomography. Afterward, the reconstructed isoconcentration mapping was applied to identify Mg-rich clusters. The density and average size of the Mg clusters were estimated to be approximately 4.3 × 10 cm and 5 nm, respectively. Excluding the Mg atoms contained in the clusters, the remaining Mg doping concentration in the p-GaN region was calculated to be 1.1 × 10 cm. Despite the lack of effective activation, a reasonably low operating voltage and distinct light emissions were preliminarily observed in MQS nanowire-based LEDs under the optimal n-GaN cap growth conditions. In the fabricated MQS-nanowire devices, carriers were injected into both the -plane and -plane of the nanowires without a clear quantum confinement Stark effect.